Adjusting the microstructure through the deformation process is one of the ways to improve the properties of Mg alloys. Most studies have focused on the influence of the microstructure after deformation treatment on the mechanical properties of Mg alloys. In this paper, extruded and forged Mg-Gd-Y-Nd-Zr alloys were selected to investigate the corrosion performance of two deformed magnesium alloys immersed in 0.6 M NaCl solution using a hydrogen evolution test, a weight loss test, an immersion experiment, and an electrochemical test. The results showed that WE43 alloys undergoing different deformation treatments presented different microstructures, which led to different corrosion behaviors and corrosion resistance. The extruded WE43 alloy showed uniform corrosion, while the forged WE43 alloy suffered severe local galvanic corrosion. Meanwhile, the corrosion rate of the forged WE43 alloy was about four times faster than that of the extruded WE43 alloy.

A layered gradient aluminum foam was prepared by powder sintering with sodium thiosulfate (Na₂S₂O₃) particles as the cell-forming agent. By cutting, polishing and observing under a microscope, it was found that the aluminum powder particles were not completely melted after sintering but were only combined by surface melting. Based on the quasi-static compression test and the macroscopic diagram of the sample during deformation, the mechanical properties of gradient aluminum foam were studied, and their deformation characteristics and mechanism were analyzed and discussed.

Aluminum foam that is lightweight with high specific strength, high energy absorption and other characteristics can be used in aerospace, transportation, machinery manufacturing and other fields. The PCM method is usually used to prepare closed-cell aluminum foams. The microsized aluminum foams made by this process can solve the non-uniform pore structures caused by liquid drainage during the foaming process of large aluminum foams. The surface morphology and internal pore structure of microsized aluminum foams are affected by the quality of the precursor used for foaming. In this paper, foamable precursors were obtained via either hot rolling or hot extrusion and subsequently foamed. By analyzing the micromorphology and foaming process of the precursor, the influence of the technological method on the macroscopic pore structure of the final aluminum foam was studied. The results show that the aluminum powder particles in the precursor prepared with the hot rolling method had metallurgical bonding, and the outer surface was dense, with almost no porosity and holes in the interior. The microsized aluminum foam obtained after foaming was smooth in appearance, and the internal pore structure was round and uniform. The reason is that during the foaming process of microsize aluminum foam, the foaming agent was evenly distributed in the precursor of the hot rolling process because of its compact structure. During the foaming process, the decomposed gas of the foaming agent will not escape, and the evenly distributed foaming agent tends to nucleate in situ. In the process of rapid foaming, the pressure in the bubble is enough to resist the liquid drainage phenomenon caused by gravity, and the growth direction of the gas core is isotropic, which promotes the foam structure to be more rounded and uniform.

The space holder method, a kind of powder metallurgy method which can avoid the process of melting metal to prepare metal foams, has particular significance in solving the difficulty of preparing metal foams with high melting points. In this paper, Na₂S₂O₃·5H₂O, a novel space holder, was used to prepare aluminium foam and copper foam, which were then used to test the heat dissipation performance of the metal foams. We first prepared two kinds of cell structures for (spherical cell and composite cells) aluminium and copper foam, then, we compared the performances of their heat dissipation, and it was found that both the spherical cell metal foam and composite cell metal foam promoted heat dissipation in the environment of natural convection, and the difference between them was not apparent. In the environment of forced convection, the composite porous metal showed a better heat dissipation performance.