Excessive reservoir water poses significant challenges in the oil and gas industry by diminishing hydrocarbon recovery efficiency and generating environmental and economic complications. Conventional polymer flooding techniques, although beneficial, often prove inadequate under conditions of elevated temperature and salinity, highlighting the need for more resilient materials. In this research, two types of acrylamide-based preformed particle gels (PPGs) were synthesized, as follows: polyelectrolyte and polyampholyte. These PPGs were engineered to improve plugging efficiency and endure extreme reservoir environments. The polyelectrolyte gels were synthesized using acrylamide (AAm) and sodium acrylate (SA), while the polyampholyte gels incorporated AAm, AMPS, and APTAC, with crosslinking achieved through MBAA. The swelling properties, modulated by temperature, salinity, and pH, were evaluated using the Ritger–Peppas and Yavari–Azizian models. The mechanical characteristics and surface morphology of the gels were analyzed using SEM and BET techniques. In sand pack experiments designed to mimic high-permeability reservoirs, the inclusion of 0.5 wt.% of fine PPGs substantially reduced water permeability, outperforming traditional hydrogels. Notably, the polyampholyte PPGs demonstrated superior resilience and efficacy in plugging. However, the experiments were limited by the low test temperature (25 °C) and brine salinity (26.6 g/L). Future investigations will aim to apply these PPGs in high-temperature, fractured carbonate reservoirs.

Polyampholyte nanogels based on N-isopropylacrylamide (NIPAM), (3-acrylamidopropyl) trimethylammonium chloride (APTAC) and 2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt (AMPS) were synthesized via conventional redox-initiated free radical copolymerization. The resultant nanogels of various compositions, specifically [NIPAM]:[APTAC]:[AMPS] = 90:5:5; 90:7.5:2.5; 90:2.5:7.5 mol.%, herein abbreviated as NIPAM₉₀-APTAC₅-AMPS₅, NIPAM₉₀-APTAC_7.5-AMPS_2.5 and NIPAM₉₀-APTAC_2.5-AMPS_7.5, were characterized by a combination of ¹H NMR and FTIR spectroscopy, TGA, UV–Vis, DLS and zeta potential measurements. The temperature and salt-responsive properties of amphoteric nanogels were studied in aqueous and saline solutions in a temperature range from 25 to 60 °C and at ionic strengths (μ) of 10⁻³ to 1M NaCl. Volume phase transition temperatures (VPTT) of the charge-balanced nanogel were found to reach a maximum upon the addition of salt, whereas the same parameter for the charge-imbalanced nanogels exhibited a sharp decrease at higher saline concentrations. A wide bimodal distribution of average hydrodynamic sizes of nanogel particles had a tendency to transform to a narrow monomodal peak at elevated temperatures and higher ionic strengths. According to the DLS results, increasing ionic strength results in the clumping of nanogel particles.

Preformed particle gels (PPGs) based on acrylamide (AAm), (3-acrylamidopropyl) trimethylammonium chloride (APTAC), and 2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt (AMPS) were synthesized via conventional free radical copolymerization. The resultant PPGs of various compositions were characterized using FTIR spectroscopy, TG and DT analysis, and mechanical testing. The swelling behavior of PPGs depending on ionic strength, temperature, degree of crosslinking, and pH was also studied. The obtained results show that the swelling mechanism of PPGs is mainly due to the diffusion of the solvent. The mechanical properties of PPGs were improved by creating a composite polymer network by adding the clay mineral (bentonite) to the reaction mixture of monomers, which also makes it possible to control the Young’s modulus and the swelling degree of the samples.

Multilayer films were synthesized from a complex of branched polyethyleneimine (PEI) with copper nanoparticles (PEI-CuNPs) and sodium poly-2-acrylamide-2-methyl-1-propanesulfonate (PAMPSNa), applied layer-by-layer (LbL) on a solid support in an acidic medium. Protonation of the amino groups of PEI in an acidic medium increases the positive charge of the PEI-CuNPs system to +43.5 mV and promotes the formation of an interpolyelectrolyte complex between the positively charged PEI-CuNPs and the highly charged anionic polyelectrolyte PAMPS, the ζ-potential of which was -141 mV. AFM images and SEM micrographs showed a uniform distribution of spherical copper nanoparticles in the homogeneous structure of the multilayer film. The optical characteristics and hydrodynamic dimensions of PEI-CuNPs indicate the formation of PEI-CuNPs nanoparticles with sizes of 60-300 nm, with an average size of up to 100 nm. Copper nanoparticles distributed uniformly in a multilayer PEI-CuNPs/PAMPS film may be of interest for applications in the field of membrane catalysis, biochips, sensor membranes, and controlled drug delivery.