This paper presents the viscosifying and oil recovery efficiencies of a novel high-molecular-weight ternary polyampholyte (TPA), composed of 80 mol.% acrylamide (AAm) (a nonionic monomer), 10 mol.% 2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt (AMPS) (an anionic monomer), and 10 mol.% (3-acrylamidopropyl) trimethylammonium chloride (APTAC) (a cationic monomer), in various high-salinity brines as compared to the efficiency of hydrolyzed poly(acrylamide) (HPAM), which is the most commonly used polymer in oil production. The results show that, in a range of salinity from 200 to 300 g∙L⁻¹, the viscosity of the TPA solution is rather high and relatively stable, whereas that of HPAM severely decreases. The ability of TPA to increase its viscosity in extremely high salinity brines is explained by the antipolyelectrolyte effect, resulting in the unfolding of macromolecular chains of charge-balanced polyampholytes at a quasi-neutral state, which occurs due to the screening of the electrostatic attraction between oppositely charged moieties. The novelty of this research is that, in high-salinity reservoirs, the amphoteric terpolymer Aam-AMPS-APTAC may surpass HPAM in oil displacement capability.

Polyampholyte nanogels based on N-isopropylacrylamide (NIPAM), (3-acrylamidopropyl) trimethylammonium chloride (APTAC) and 2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt (AMPS) were synthesized via conventional redox-initiated free radical copolymerization. The resultant nanogels of various compositions, specifically [NIPAM]:[APTAC]:[AMPS] = 90:5:5; 90:7.5:2.5; 90:2.5:7.5 mol.%, herein abbreviated as NIPAM₉₀-APTAC₅-AMPS₅, NIPAM₉₀-APTAC_7.5-AMPS_2.5 and NIPAM₉₀-APTAC_2.5-AMPS_7.5, were characterized by a combination of ¹H NMR and FTIR spectroscopy, TGA, UV–Vis, DLS and zeta potential measurements. The temperature and salt-responsive properties of amphoteric nanogels were studied in aqueous and saline solutions in a temperature range from 25 to 60 °C and at ionic strengths (μ) of 10⁻³ to 1M NaCl. Volume phase transition temperatures (VPTT) of the charge-balanced nanogel were found to reach a maximum upon the addition of salt, whereas the same parameter for the charge-imbalanced nanogels exhibited a sharp decrease at higher saline concentrations. A wide bimodal distribution of average hydrodynamic sizes of nanogel particles had a tendency to transform to a narrow monomodal peak at elevated temperatures and higher ionic strengths. According to the DLS results, increasing ionic strength results in the clumping of nanogel particles.

Preformed particle gels (PPGs) based on acrylamide (AAm), (3-acrylamidopropyl) trimethylammonium chloride (APTAC), and 2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt (AMPS) were synthesized via conventional free radical copolymerization. The resultant PPGs of various compositions were characterized using FTIR spectroscopy, TG and DT analysis, and mechanical testing. The swelling behavior of PPGs depending on ionic strength, temperature, degree of crosslinking, and pH was also studied. The obtained results show that the swelling mechanism of PPGs is mainly due to the diffusion of the solvent. The mechanical properties of PPGs were improved by creating a composite polymer network by adding the clay mineral (bentonite) to the reaction mixture of monomers, which also makes it possible to control the Young’s modulus and the swelling degree of the samples.

In our previous papers [1, 2] we considered the behavior of linear and crosslinked polyampholytes based on fully charged anionic monomer — 2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt (AMPS) and cationic monomer — (3-acrylamidopropyl)trimethylammonium chloride (APTAC) in aqueous-salt solutions, swelling and mechanical properties. In the present paper we report the applicability of salt tolerant amphoter-ic terpolymers composed of AMPS, APTAC and acrylamide (AAm) in enhanced oil recovery (EOR). The amphoteric terpolymers of different compositions, particularly [AAm]:[AMPS]:[APTAC] = 50:25:25; 60:20:20; 70:15:15; 80:10:10 and 90:5:5 mol.% were prepared by free-radical polymerization, identified and their viscosifying ability with respect to reservoir saline water (salinity is 163 g⋅L-1) at 60 °C was tested. It was found that due to polyampholytic nature, the AAm-AMPS-APTAC terpolymers exhibited improved viscosifying behavior at high salinity water. As a result, the appropriate salt tolerant sample [AAm]:[AMPS]:[APTAC] = 80:10:10 mol.% was selected for polymer flooding experiments. Polymer flood-ing experiments on high permeable sand pack model demonstrated that only 0.5 % oil was recovered by am-photeric terpolymer. While injection of polyampholyte solution into preliminarily water flooded core sample resulted in the increase of oil recovery up to 4.8–5 %. These results show that under certain conditions the amphoteric terpolymers have a decent oil displacement ability.

High molecular weight amphoteric terpolymer based on a nonionic monomer, acrylamide (AAm), an anionic monomer, 2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt (AMPS), and a cationic monomer, (3-acrylamidopropyl) trimethylammonium chloride (APTAC), was prepared using free-radical copolymerization in an aqueous solution and characterized by ¹H NMR, FTIR, GPC, DLS, zeta potential and viscometry. The polymer was shown to be viscosifying, and therefore can be utilized as a polymer flooding agent in the high salinity and temperature conditions of oil reservoirs. Injection of 0.25 wt.% of amphoteric terpolymer, dissolved in 200-300 g∙L^-1 brine, into high and low permeability sand pack models demonstrated that the oil recovery factor (ORF) increases by up to 23-28% in comparison with saline water flooding. This is explained by an increase in the viscosity of brine solution due to disruption of intra- and interionic contacts between oppositely charged AMPS and APTAC moieties, demonstrating the antipolyelectrolyte effect. In high saline water, the anions and cations of salts screen the electrostatic attraction between positively and negatively charged macroions, resulting in expansion of the macromolecule. This phenomenon leads to an increase in the viscosifying effect on the brine solution, thus decreasing the mobility factor (M), which is defined as the ratio of displacing phase mobility (water) to displaced phase mobility (oil).