Microwave curing technology has been widely used in resin and its composite materials. In order to study its effect for curing unsaturated polyester resin (UPR) composites containing calcium carbonate (CaCO₃) filler, this paper first investigated the influence of microwave power and microwave irradiation time on the curing characteristics of UPR. Then, CaCO₃ particles were added to the UPR to investigate the microwave curing effect of the UPR composites containing the CaCO₃. The results showed that microwave irradiation could heat the UPR sample evenly, and rapidly cause the chain growth reaction, thus greatly shortening the curing time. The curing degree and products of the samples after microwave curing were consistent with that of the thermal curing. The addition of CaCO₃ particles could increase the heating rate of the UPR composites, which would accelerate the curing rate of the UPR. However, higher microwave power could lead to pore defects inside the UPR composites with higher CaCO₃ content, resulting in a lower strength. Thus, the compactness of the samples should be improved by reducing the microwave power and prolonging the microwave treatment time.

The adhesion of water to the surfaces of unmanned aerial vehicles (UAVs) adversely affects the function. The proposed UAVs will have underwater as well as flight capability, and these aquatic UAVs must shed water to resume flight. The efficient separation of the adhering water from aquatic-UAV surfaces is a challenging problem; we investigated the application of hydrophobic surfaces as a potential solution. Using aquatic-UAV models, one with hydrophilic surfaces and the other with superhydrophobic anisotropic textured surfaces, the antiwetting mechanism of the hydrophobic surfaces was investigated using a simulated-precipitation system and instrumentation to measure the load of the water adhering to the aquatic UAV, and to measure the impact energies. When the model was stationary (passive antiwetting), no adhesion occurred on the superhydrophobic surfaces, while continuous asymmetric thick liquid films were observed on the hydrophilic surfaces. The superhydrophobic surfaces reduced the rain loading by 87.5%. The vibration and movement of the model (dynamic antiwetting, simulating flight motions) accelerated the separation process and reduced the contact time. The observed results were augmented by the use of computational fluid dynamics with lattice Boltzmann methods (LBM) to analyze the particle traces inside the droplets, the liquid phase velocity-field and pressure-field strengths, and the backward bouncing behavior of the derived droplet group induced by the moving surface. The synergy between the superhydrophobic surfaces and the kinetic energy of the droplets promotes the breakup of drops, which avoids the significant lateral unbalance observed with hydrophilic surfaces during simulated flight.

In this article, aiming at the problems of low mechanical properties and the unstable structure of the binder in inorganic artificial stone, performance improvements were studied. The effects of 12 materials of blast-furnace slag (BFS), fly ash (FA), and kaolin on the properties and microstructure of inorganic binders were systematically studied and analyzed. As a result, the compressive strength of BFS-2, FA-1, and FA-2 binder was increased by 10.0, 6.0, and 1.5%, and the flexural strength was increased by 44.8, 79.2, and 1.3%, respectively. It was worth noting that BFS and FA could effectively promote hydration reactions due to active materials and boost the growth of C–S–H and CH, leading to the inorganic binder forming a stable structure. Thus, this work systematically designs and prepares inorganic binders with high compressive strength and excellent flexural strength. This reveals how inorganic materials affect the properties of inorganic binders on the microstructure and offer a new idea for the development of this field.

Traditional marine antifouling coatings function through releasing toxic antifouling agents, causing serious harm to marine ecosystems. To address this challenge, an eco-friendly fluoro-silicon-modified polythiourethane (FSi-PTU) coating has been prepared via a polymerization reaction with dihydroxy propyl silicone oil (HO-PDMS-OH), 1H,1H,2H,2H-perfluorohexanol (FTOH), hexamethylene diisocyanate (HDI), and pentaerythritol tetrakis (3-mercaptopropionate) (PETMP). The FSi-PTU polymer incorporates siloxane segments and fluorinated side chains, which are inhomogeneously distributed on the coating surface and construct a hydrophobic surface. The FSi-PTU coating exhibits good hydrophobicity, strong adhesion (≥2.14 MPa), and improved mechanical properties. The antifouling properties of the FSi-PTU coating have been researched. The results of laboratory tests demonstrate that the FSi-PTU coating exhibits excellent anti-protein adsorption and anti-algal attachment performance. The FSi-PTU-2 coating shows certain antifouling properties in the actual seawater test for three months. The results provide a certain reference value for developing eco-friendly marine antifouling coatings.

Star anise, a member of the Illiciaceae family within the dicotyledonous Magnoliophyta, is also known as Chinese star anise.[1] It is a plant of significant economic value, primarily grown in the s...