An atomic force microscope colloidal probe technique has been employed to probe normal and friction forces between silica surfaces coated with adsorbed layers of a diblock copolymer of the composition poly(N-isopropylacrylamide)₄₈-block-poly(3-acrylamidopropyl)trimethylammonium chloride)₂₀, abbreviated PNIPAAM₄₈-b-PAMPTMA(+)₂₀. The interactions between the PNIPAAM₄₈-b-PAMPTMA(+)₂₀-coated surfaces across a 0.1 mM NaCl (pH 6) solution at 25 °C are purely repulsive, due to a combination of steric and electrostatic double-layer forces. However, when the temperature is increased to 35 °C, and subsequently to 45 °C, an attractive force develops at short separations due to the unfavourable PNIPAAM–water interaction at these temperatures. The temperature-dependent polymer–water interaction has implications for the friction force between the layers. At 25 °C a frictional force that increases linearly with increasing load is observed once the surfaces are brought into close contact. At higher temperatures significantly higher friction forces appear as a consequence of attractive segment–segment interactions. Further, a clearly expressed hysteresis between friction forces encountered on loading and unloading is detected. Our results demonstrate that both normal and friction forces between surfaces can be controlled by temperature changes when temperature-responsive polymers are employed, and friction forces can be adjusted as required from low to high.

Phospholipids and hyaluronan have been implied to fulfil important roles in synovial joint lubrication. Since both components are present in synovial fluid, self-assembly structures formed by them should also be present. We demonstrate by small angle X-ray scattering that hyaluronan associates with the outer shell of dipalmitoylphophatidylcholine (DPPC) vesicles in bulk solution. Further, we follow adsorption to silica from mixed hyaluronan/DPPC vesicle solution by Quartz Crystal Microbalance with Dissipation measurements. Atomic Force Microscope imaging visualises the adsorbed layer structure consisting of non-homogeneous phospholipid bilayer with hyaluronan/DPPC aggregates on top. The presence of these aggregates generates a long-range repulsive surface force as two such surfaces are brought together. However, the aggregates are easily deformed, partly rearranged into multilayer structures and partly removed from between the surfaces under high loads. These layers offer very low friction coefficient (<0.01), high load bearing capacity (≈23MPa), and self-healing ability. Surface bound DPPC/hyaluronan aggregates provide a means for accumulation of lubricating DPPC molecules on sliding surfaces.

In living organisms the aqueous medium is used for providing low friction forces. This is achieved by synergistic actions of different biomolecules that together accomplish a high load bearing capacity and sustain an easily sheared water layer.

Phospholipids fulfill an important role in joint lubrication. They, together with hyaluronan and glycoproteins, are the biolubricants that sustain low friction between cartilage surfaces bathed in synovial fluid. In this work we have investigated how the friction force and load bearing capacity of 1,2-dipalmitoyl-sn-glycero-3-phosphocholine (DPPC) bilayers on silica surfaces are affected by temperature, covering the temperature range 25-52°C. Friction forces have been determined utilizing the AFM colloidal probe technique, which showed that DPPC bilayers are able to provide low friction forces over the whole temperature interval. However, the load bearing capacity is improved at higher temperatures. We interpret this finding as being a consequence of lower rigidity and higher self-healing capacity of the DPPC bilayer in the liquid disordered state compared to the gel state. The corresponding structure of solid supported DPPC bilayers at the silica-liquid interface has been followed using X-ray reflectivity measurements, which suggests that the DPPC bilayer is in the gel phase at 25°C and 39°C and in the liquid disordered state at 55°C. Well-defined bilayer structures were observed for both phases. The deposited DPPC bilayers were also imaged using AFM PeakForce Tapping mode, and these measurements indicated a less homogeneous layer at temperatures below 37°C.

Synovial surfaces are lubricated by biomolecular aggregates that act in synergy, and lubricin is one key biolubricant. Its molecular structure allows extensive hydration and this is conducive to its lubrication performance. However, in order to fullfil its lubrication function it needs to be anchored and oriented on the surface in a proper way. We suggest that cartilage oligomeric matrix protein (COMP) is one of the biomolecules that promotes anchoring of lubricin in a fashion that facilitates lubrication. Weakly hydrophobic poly(methyl methacrylate) (PMMA) surfaces were coated by COMP and lubricin, individually and in combinations. Adsorption was investigated using a quartz crystal microbalance, and friction between the biopolymer-coated surfaces was determined by employing the atomic force microscope-colloidal probe technique. It was found that COMP facilitated firm directed attachment of lubricin in a manner that resulted in low friction forces, significantly lower than what was achieved when lubricin was directly adsorbed to PMMA. Evidently, COMP provides means for lubricin to attach strongly and in a favourable conformation for efficient lubrication of this surface. We suggest that our findings can be extrapolated to cartilage surfaces, where co-localization of COMP and lubricin has been demonstrated.

Interfacial properties of two types of mucins have been investigated at the aqueous solution/poly(methyl methacrylate) (PMMA) interface. One is commercially available bovine submaxillary mucin, BSM, which consists of alternating glycosylated and nonglycosylated regions. The other one is a recombinant mucin-type fusion protein, PSGL-1/mIgG_2b, consisting of a glycosylated mucin part fused to the Fc part of an immunoglobulin. PSGL-1/mIgG_2b is mainly expressed as a dimer upon production. A quartz crystal microbalance with dissipation was used to study the adsorption of the mucins to PMMA surfaces. The mass of the adsorbed mucin layers, including the adsorbed mucin and water trapped in the layer, was found to be significantly higher for PSGL-1/mIgG_2b than for BSM. Atomic force microscopy with colloidal probe was employed to study interactions and frictional forces between mucin-coated PMMA surfaces. Purely repulsive forces of steric origin were observed between PSGL-1/mIgG_2b mucin layers, whereas a small adhesion was detected between BSM layers and attributed to bridging. Both mucin layers reduced the friction force between PMMA surfaces in aqueous solution. The reduction was, however, significantly more pronounced for PSGL-1/mIgG_2b. The effective friction coefficient between PSGL-1/mIgG_2b-coated PMMA surfaces is as low as 0.02 at low loads, increasing to 0.24 at the highest load explored, 50 nN. In contrast, a friction coefficient of around 0.7 was obtained between BSM-coated PMMA surfaces. The large differences in interfacial properties for the two mucins are discussed in relation to their structural differences.