Well-dispersed fish gelatin-based nanocomposites were prepared by adding ZnO nanorods (NRs) as fillers to aqueous gelatin. The effects of ZnO NR fillers on the mechanical, optical, and electrical properties of fish gelatin bio-nanocomposite films were investigated. Results showed an increase in Young's modulus and tensile strength of 42% and 25% for nanocomposites incorporated with 5% ZnO NRs, respectively, compared with unfilled gelatin-based films. UV transmission decreased to zero with the addition of a small amount of ZnO NRs in the biopolymer matrix. X-ray diffraction showed an increase in the intensity of the crystal facets of (10ī1) and (0002) with the addition of ZnO NRs in the biocomposite matrix. The surface topography of the fish gelatin films indicated an increase in surface roughness with increasing ZnO NR concentrations. The conductivity of the films also significantly increased with the addition of ZnO NRs. These results indicated that bio-nanocomposites based on ZnO NRs had great potentials for applications in packaging technology, food preservation, and UV-shielding systems.

This study examines the dielectric properties of filled PVDF film and filled PVDF-TrFE film incorporated with 1, 3, 5, and 7 weight percentages of magnesium oxide (MgO) nanofillers. The metal-insulator-metal (MIM) configuration demonstrates PVDF/MgO with 7 weight percent of MgO which produced high dielectric constant (1 kHz) with low dielectric loss. The ATR-FTIR spectra of PVDF/MgO (7%) indicate wide bonding peaks at 840 cm^-1 and 880 cm^-1, assigned to -CH₂ and -CF₂ groups, respectively. This implies the presence of high content of β-crystals in the PVDF/MgO (7%) film. A shift in the peak was observed in the same film, from 1170 cm^-1 to 1180 cm^-1 suggesting possible transformation from γ-crystals to β-crystals. This film showed no apparent defect on its film surface. Thus, it established that PVDF incorporated with 7% MgO can be used to produce nanocomposite thin film for low-frequency electronic devices.