For the first time, a study of the influence of the molecular weight of the thermoplastic partially crystalline polyimide R-BAPB on the thermophysical and mechanical properties of carbon plastics was presented. The molecular weight of polyimide was determined using the method of light scattering and the study of the intrinsic viscosity of polyamic acid solutions. To obtain CFRPs, the uniform distribution of polyimide powder on continuous carbon fibers via electrostatic spraying and further hot calendering and pressing were applied. The study of the structure of the obtained carbon plastics via scanning electron microscopy has shown that the growth of the molecular weight of polyimide prevents the impregnation of carbon fiber with the introduced polyimide. Moreover, an increase in the molecular weight of polyimide leads to a rise in glass transition and thermal decomposition temperatures up to 590 °C, while the degree of crystallinity of CFRP falls. Nonetheless, raising the molecular weight from 22,000 to 70,000 g/mol of a binder polymer improves the interlayer fracture toughness G_1C by more than five times.

Biocompatible electrically conducting chitosan-based films filled with single-wall carbon nanotubes were obtained. Atomic force microscopic studies of the free surface topography revealed a change in the morphology of chitosan films filled with single-wall carbon nanotubes. Introducing 0.5 wt.% of single-wall carbon nanotubes into chitosan results in an increase in tensile strength of the films (up to ~180 MPa); the tensile strain values also rise up to ~60%. It was demonstrated that chitosan films containing 0.1–3.0 wt.% of single-wall carbon nanotubes have higher conductivity (10 S/m) than pure chitosan films (10⁻¹¹ S/m). The investigation of electrical stimulation of human dermal fibroblasts on chitosan/single-wall carbon nanotubes film scaffolds showed that the biological effect of cell electrical stimulation depends on the content of single-walled carbon nanotubes in the chitosan matrix.

Three-dimensional (3D) bioprinting opens up many possibilities for tissue engineering, thanks to its ability to create a three-dimensional environment for cells like an extracellular matrix. However, the use of natural polymers such as silk fibroin in 3D bioprinting faces obstacles such as having a limited printability due to the low viscosity of such solutions. This study addresses these gaps by developing highly viscous, stable, and biocompatible silk fibroin-based inks. The addition of 2% carboxymethyl cellulose sodium and 1% sodium alginate to an aqueous solution containing 2.5 to 5% silk fibroin significantly improves the printability, stability, and mechanical properties of the printed scaffolds. It has been demonstrated that the more silk fibroin there is in bioinks, the higher their printability. To stabilize silk fibroin scaffolds in an aqueous environment, the printed structures must be treated with methanol or ethanol, ensuring the transition from the silk fibroin’s amorphous phase to beta sheets. The developed bioinks that are based on silk fibroin, alginate, and carboxymethyl cellulose demonstrate an ease of printing and a high printing quality, and have a sufficiently good biocompatibility with respect to mesenchymal stromal cells. The printed scaffolds have satisfactory mechanical characteristics. The resulting 3D-printing bioink composition can be used to create tissue-like structures.

In this work, an electrically conductive composite based on thermoplastic polyimide and graphene was obtained and used as a bioelectrode for electrical stimulation of human dermal fibroblasts. The values of the electrical conductivity of the obtained composite films varied from 10⁻¹⁵ to 10² S/m with increasing graphene content (from 0 to 5.0 wt.%). The characteristics of ionic and electronic currents flowing through the matrix with the superposition of cyclic potentials ± 100 mV were studied. The high stability of the composite was established during prolonged cycling (130 h) in an electric field with a frequency of 0.016 Hz. It was established that the composite films based on polyimide and graphene have good biocompatibility and are not toxic to fibroblast cells. It was shown that preliminary electrical stimulation increases the proliferative activity of human dermal fibroblasts in comparison with intact cells. It is revealed that an electric field with a strength E = 0.02–0.04 V/m applied to the polyimide films containing 0.5–3.0 wt.% of the graphene nanoparticles activates cellular processes (adhesion, proliferation).