To address the challenge of balancing the mechanical, thermal insulation, and flame-retardant properties of building insulation materials, this study presented a facile approach to modify the rigid polyurethane foam composites (RPUFs) via commercial expandable graphite (EG), ammonium polyphosphate (APP), and silica aerogel (SA). The resulting EG/APP/SA/RPUFs exhibited low thermal conductivity close to neat RPUF. However, the compressive strength of the 6EG/2APP/SA/RPUF increased by 49% along with achieving a V-0 flame retardant rating. The residual weight at 700 °C increased from 19.2 wt.% to 30.9 wt.%. Results from cone calorimetry test (CCT) revealed a 9.2% reduction in total heat release (THR) and a 17.5% decrease in total smoke production (TSP). The synergistic flame-retardant mechanism of APP/EG made significant contribution to the excellent flame retardant properties of EG/APP/SA/RPUFs. The addition of SA played a vital role in reducing thermal conductivity and enhancing mechanical performance, effectively compensating for the shortcomings of APP/EG. The cost-effective EG/APP/SA system demonstrates a positive ternary synergistic effect in achieving a balance in RPUFs properties. This study provides a novel strategy aimed at developing affordable building wall insulation material with enhanced safety features.

In this study, desert sand was used as supplementary materials in alkali-activated cements (AAC) with granulated blast furnace slag (GBFS) and fly ash (FA). For the first time, a systematic investigation was conducted on the effects of various treatment methods and contents of desert sand on the strength and microstructure of AAC. This study also analyzed the X-ray diffractometer (XRD), Scanning Electron Microscopy-Energy Dispersive X-ray Microanalysis (SEM-EDX), Mercury Intrusion Porosimetry (MIP), pH values, and Fourier-transform infrared spectroscopy (FT-IR) properties of AAC pastes containing differently treated desert sand to uncover the mechanisms by which these treatments and dosages influence mechanical properties of AAC. Untreated desert sand (DS), temperature-treated desert sand (DS-T), and ground desert sand for two different durations (20 mins and 30 mins) all exhibited some pozzolanic activity but primarily acted as fillers in the AAC pastes. Among the samples, DS-T demonstrated the highest pozzolanic activity, though it was still less than that of fly ash (FA). The optimal dosage for the modified desert sands was determined to be 10%. However, The optimal dosage of different modified desert sands is 10%. The flexural strength of DS-G30-10 reaches 6.62 MPa and the compressive strength reaches 72.3 MPa, showing the best comprehensive mechanical properties.

The study investigated the effects of a toughening agent and micron-sized toughening particles (TP) on the resin and carbon fiber-reinforced polymer (CFRP) composites, with a particular focus on compressive strength. The results showed that the addition of the toughening agent improved the overall mechanical properties of both the resin and CFRP but had a minor effect on the residual compressive strength (CAI) of CFRP after impact. Compared to the pure toughening agent, the addition of TP increased the CAI, GIC, and GIIC of CFRP by 74%, 35%, and 68%, respectively. The SEM, ultrasonic C-scan, and metallographic microscopy were used to analyze the failure morphology and TP distribution. Compared to pure toughening agent modification, the introduction of TP led to the formation of continuous toughening particle layers, which reduced the compression damage area by 61%, significantly balancing and absorbing the load. This modification also resulted in typical kink band damage. This study found that resin toughening significantly improved the compressive strength of CFRP, while micron-sized toughening particles, in the form of toughening layers, notably improved the CAI. These findings provide valuable insights for enhancing the compression and impact resistance of CFRP.

This study is dedicated to the development of a new type of cesium tungsten bronze energy-saving laminated glass and explores its application in insulating glass combinations, offering innovative ideas and practical solutions for advancing energy-saving glass technology. Experimental results show that both Cs_xWO₃ (CWO) dispersions exhibit good visible light transmittance and near-infrared shielding properties, with CWO1 demonstrating superior shielding in the 650–950 nm range, attributed to differences in shape and size distribution and verified by simulations using the Drude–Lorentz model and the finite element method.