Polymer-dispersed liquid crystal (PDLC) films were prepared by the ultraviolet-light-induced polymerization of photopolymerizable monomers in nematic liquid crystal/chiral dopant/thiol-acrylate reaction monomer composites. The effects of the chiral dopant and crosslinking agents on the electro-optical properties of the PDLC films were systematically investigate. While added the chiral dopant S811 into the PDLC films, the initial off-state transmittance of the films was decreased. It was found that the weight ratio among acrylate monomers, thiol monomer PETMP and the polymercaptan Capcure 3-800 showed great influence on the properties of the fabricated PDLC films because of the existence of competition between thiol-acrylate reaction and acrylate monomer polymerization reaction. While adding polymercaptans curing agent Capcure 3-800 with appropriate concentration into the PDLC system, lower driven voltage and higher contrast ratio were achieved. This made the polymer network and electro-optical properties of the PDLC films easily tunable by the introduction of the thiol monomers.

In this study, a polymer dispersed cholesteric liquid crystal (PDChLC) film obtained via a one-step fabrication technique based on photopolymerization of a thiol-acrylate reaction system was prepared and characterized for the first time. The effects of the chiral dopant, the influence of thiol monomer functionality and content on the morphology and subsequent performance of the PDChLC films were systematically investigated. It was demonstrated that the addition of a small amount of chiral dopant slightly increased the driving voltage, but decreased the off-state transmittance significantly. Furthermore, scanning electron micrographs (SEM) shown that the liquid crystal (LC) droplet size decreased at first and then increased with the increasing amount of thiol monomer functionality, while increasing the thiol content increased the LC droplet size. Correspondingly, the electro-optical switching behavior was directly dependent on LC droplet size. By tuning the raw material composition, PDChLC film with optimized electro-optical performance was prepared.