This Review highlights basic and transition metal conducting and semiconducting oxides. We discuss their material and electronic properties with an emphasis on the crystal, electronic, and band structures. The goal of this Review is to present a current compilation of material properties and to summarize possible uses and advantages in device applications. We discuss Ga2O3, Al2O3, In2O3, SnO2, ZnO, CdO, NiO, CuO, and Sc2O3. We outline the crystal structure of the oxides, and we present lattice parameters of the stable phases and a discussion of the metastable polymorphs. We highlight electrical properties such as bandgap energy, carrier mobility, effective carrier masses, dielectric constants, and electrical breakdown field. Based on literature availability, we review the temperature dependence of properties such as bandgap energy and carrier mobility among the oxides. Infrared and Raman modes are presented and discussed for each oxide providing insight into the phonon properties. The phonon properties also provide an explanation as to why some of the oxide parameters experience limitations due to phonon scattering such as carrier mobility. Thermal properties of interest include the coefficient of thermal expansion, Debye temperature, thermal diffusivity, specific heat, and thermal conductivity. Anisotropy is evident in the non-cubic oxides, and its impact on bandgap energy, carrier mobility, thermal conductivity, coefficient of thermal expansion, phonon modes, and carrier effective mass is discussed. Alloys, such as AlGaO, InGaO, (AlxInyGa1−x−y)2O3, ZnGa2O4, ITO, and ScGaO, were included where relevant as they have the potential to allow for the improvement and alteration of certain properties. This Review provides a fundamental material perspective on the application space of semiconducting oxide-based devices in a variety of electronic and optoelectronic applications.

External quantum efficiency in solar cells based on junctions between PbSe quantum dots (QDs) and thin ZnO films is increased by replacing the ZnO films with a vertically oriented array of single-crystalline ZnO nanowires, and infiltrating this array with colloidal QDs. When illuminated with $100\text{mW}/{\text{cm}}^2$ of simulated solar light, QD-nanowire solar cells exhibited power conversion efficiencies approaching 2%, approximately three times higher than that achieved with thin-film ZnO devices constructed with the same amount of QDs. Significant photocurrent and power conversion improvement with increasing nanowire length is consistent with higher exciton and charge collection efficiencies.

β-Ga2O3 is an emerging ultra-wide bandgap semiconductor, holding a tremendous potential for power-switching devices for next-generation high power electronics. The performance of such devices strongly relies on the precise control of electrical properties of β-Ga2O3, which can be achieved by implantation of dopant ions. However, a detailed understanding of the impact of ion implantation on the structure of β-Ga2O3 remains elusive. Here, using aberration-corrected scanning transmission electron microscopy, we investigate the nature of structural damage in ion-implanted β-Ga2O3 and its recovery upon heat treatment with the atomic-scale spatial resolution. We reveal that upon Sn ion implantation, Ga2O3 films undergo a phase transformation from the monoclinic β-phase to the defective cubic spinel γ-phase, which contains high-density antiphase boundaries. Using the planar defect models proposed for the γ-Al2O3, which has the same space group as β-Ga2O3, and atomic-resolution microscopy images, we identify that the observed antiphase boundaries are the {100}1/4 ⟨110⟩ type in cubic structure. We show that post-implantation annealing at 1100 °C under the N2 atmosphere effectively recovers the β-phase; however, nano-sized voids retained within the β-phase structure and a γ-phase surface layer are identified as remanent damage. Our results offer an atomic-scale insight into the structural evolution of β-Ga2O3 under ion implantation and high-temperature annealing, which is key to the optimization of semiconductor processing conditions for relevant device design and the theoretical understanding of defect formation and phase stability.

Activation of implanted donors into a highly-resistive, nitrogen-doped homoepitaxial β-Ga2O3 has been investigated. Nitrogen acceptors with the concentration of ∼1017 cm−3 were incorporated during epitaxial growth yielding low-doped (net donor concentration <1014 cm−3) films subsequently implanted with Si, Ge, and Sn. Upon Ohmic contact formation to the implanted regions, sheet resistance values of 314, 926, and 1676 Ω/sq were measured at room temperature for the Si-, Ge-, and Sn-implanted samples, respectively. Room temperature Hall measurements resulted in sheet carrier concentrations and Hall mobilities of 2.13 × 1014 /93, 8.58 × 1013/78, and 5.87 × 1013/63 cm2/(V s), respectively, for these three donor species. Secondary ion mass spectroscopy showed a volumetric dopant concentration of approximately 2 × 1019 cm−3 for the three species, resulting in carrier activation efficiencies of 64.7%, 40.3%, and 28.2% for Si, Ge, and Sn, respectively. Temperature-dependent Hall effect measurements ranging from 15 to 300 K showed a nearly constant carrier concentration in the Si-implanted sample, suggesting the formation of an impurity band indicative of degenerate doping. With a bulk carrier concentration of 1.3 × 1019 cm−3 for the Si implanted sample, a room temperature mobility of 93 cm2/(V s) is among the highest reported in Ga2O3 with a similar carrier concentration. The unimplanted Ga2O3:N regions remained highly resistive after the surrounding areas received implant and activation anneal. These results open the pathway for fabricating Ga2O3 devices through the selective n-type doping in highly resistive epitaxial Ga2O3.