Catalytic studies hydrogen production via steam reforming of ethanol (SRE) are essential for process optimization. Likewise, selecting the ideal support for the active phase can be critical to achieve high conversion rates during the catalytic steam reforming process. In this work, copper-based catalysts were synthesized using two different supports, NaY zeolite and Nb₂O₅/Al₂O₃ mixed oxides. The materials were prepared using wet impregnation and characterized for their physicochemical properties using different analytical techniques. Differences in the catalyst morphologies were readily attributed to the characteristics of the support. The Cu/NaY catalyst exhibited a higher specific surface area (210.40 m² g⁻¹) compared to the Cu/Nb₂O₅/Al₂O₃ catalyst (26.00 m² g⁻¹), resulting in a homogeneous metal dispersion over the support surface. The obtained results showed that, at 300 °C, both the Cu/Nb₂O₅/Al₂O₃ and Cu/NaY catalysts produced approximately 50% hydrogen and 40% acetaldehyde, but with significant differences in conversion (6% and 56%, respectively). At 450 °C, a greater product distribution and a 10% higher conversion were observed when the catalyst was supported on NaY compared to Nb₂O₅/Al₂O₃. Hence, the performance of copper-based catalysts was influenced significantly by the textural properties of the support.

Catalytic studies for hydrogen production via steam reforming of ethanol (SRE) are essential for process optimization. Likewise, selecting the ideal support for the active phase can be critical to achieve high conversion rates during the catalytic steam reforming. In this work, copper-based catalysts were synthesized using two different supports, NaY zeolite and Nb2O5/Al2O3 mixed oxides. The materials were prepared using wet impregnation and characterized for their physicochemical properties using different analytical techniques. Differences in catalyst morphologies were readily attributed to the characteristics of the support. The Cu/NaY catalyst showed better textural properties than Cu/Nb2O5/Al2O3, resulting in a homogeneous metal dispersion over the support surface. Both catalytic systems were active in SRE, but Cu/NaY resulted in higher ethanol conversions compared to Cu/Nb2O5/Al2O3. Hence, the performance of copper-based catalysts was influenced significantly by the textural properties of the support.