The present study investigates the effect of stress triaxiality on mechanical behavior and fracture of Ti-5Al-2.5Sn alloy in a practical relevant strain rate range from 0.1 to 1000 s⁻¹. Tensile tests were carried out on flat smoothed and notched specimens using an Instron VHS 40/50-20 servo-hydraulic test machine. High-speed video registration was conducted by Phantom 711 Camera. Strain fields on the specimen gauge area were investigated by the digital image correlation method (DIC). The fracture surface relief was studied using digital microscope Keyence VHX-600D. Stress and strain fields during testing of the Ti-5Al-2.5Sn alloy were analyzed by the numerical simulation method. The evolution of strain fields at the investigated loading condition indicates that large plastic deformation occurs in localization bands. The alloy undergoes fracture governing by damage nucleation, growth, and coalescence in the localized plastic strain bands oriented along the maximum shear stresses. Results confirm that the fracture of near alpha titanium alloys has ductile behavior at strain rates from 0.1 to 1000 s⁻¹, stress triaxiality parameter 0.33 < η < 0.6, and temperature close to 295 K.

Bioinert metals are used for medical implants and in some industrial applications. This study was performed to detect and analyze peculiarities that appear in the temperature distributions during quasi-static tensile testing of bioinert alloys. These alloys include VT1-0 titanium, Zr-1%Nb and Ti-45%Nb in both coarse-grain (CG) and ultrafine-grain (UFG) states. The crystal structure, as well as the crystal domain and grain sizes of these alloys in the UFG state, may be different from the CG versions and identifying the thermal signatures that occur during their deformation and fracture is of interest, as it may lead to an understanding of physical processes that occur during loading. By comparing the surface temperature distributions of specimens undergoing deformation under tensile loading to the distributions at maximum temperatures it was found that the observed differences depend on the alloy type, the alloy structural state and the thermal properties of structural defects in the specimen. Macro-defects were found in some specimens of VT1-0 titanium, Zr-1Nb and Ti-45Nb alloys in both the CG and UFG states. The average tensile strength of specimens containing defects was lower than that of specimens with no defects. Infrared thermography documents change in the thermal patterns of specimens as they are deformed under tensile loading and when the load stops changing or the specimen breaks.

Predictions on the mechanical behavior of metals and alloys with a hexagonal close-packed (HCP) lattice under dynamic influences in a wide range of temperatures are in demand for solving a wide range of applied problems. This article presents new results of numerical simulation showing the general similarity of the mechanical behavior of HCP titanium, zirconium, hafnium, and beryllium alloys under dynamic loadings in a wide range of temperatures. These alloys belong to the important isomechanical subgroup of HCP alloys. A model for numerical simulation of mechanical behavior of HCP alloys under dynamic loadings in a wide temperature range was proposed. The model takes into account the change in contributions to the flow stress from the mechanisms of twinning and dislocation slip in the considered subgroup of HCP alloys. A kinetic damage model was adopted to describe the damage evolution under complex stress conditions and under dynamic loading. Thus, it was possible to increase the accuracy of predicting the dynamic fracture under tensile loads including the spall fracture.

This article investigated the mechanical behavior of Ti-6Al-4V alloy (VT6, an analog to Ti Grade 5) in the range of strain rates from 0.1 to 10³ s⁻¹. Tensile tests with various notch geometries were performed using the Instron VHS 40/50-20 servo hydraulic testing machine. The Digital Image Correlation (DIC) analysis was employed to investigate the local strain fields in the gauge section of the specimen. The Keyence VHX-600D digital microscope was used to characterize full-scale fracture surfaces in terms of fractal dimension. At high strain rates, the analysis of the local strain fields revealed the presence of stationary localized shear bands at the initial stages of strain hardening. The magnitude of plastic strain within the localization bands was significantly higher than those averaged over the gauge section. It was found that the ultimate strain to fracture in the zone of strain localization tended to increase with the strain rate. At the same time, the Ti-6Al-4V alloy demonstrated a tendency to embrittlement at high stress triaxialities.

The paper presents the experimental results of the mechanical behavior of Ti-5Al-2.5Sn alloy at high strain rates and elevated temperature. Flat smooth and notched specimens with notch radii of 10 mm, 5 mm, and 2.5 mm were used. The experimental studies were carried out using the high-velocity servo hydraulic test machine Instron VHS 40/50-20. The samples were heated with flat ceramic infrared emitters on average between 60 s and 160 s. The temperature control in the working part of specimens was carried out in real time using a chromel-alumel thermocouple. The digital image correlation (DIC) method was employed to investigate the evolution of local fields in the gauge section of the specimen. Data on the influence of stress triaxiality on the ductility of Ti-5Al-2.5Sn alloy were obtained under tension with strain rates ranging from 0.1 to 10³ s⁻¹ at a temperature of 673 K. It was found that, at 673 K, the ductility of Ti-5Al-2.5Sn alloy increases with the increasing strain rate for both smooth and notched specimens.