Bioinert metals are used for medical implants and in some industrial applications. This study was performed to detect and analyze peculiarities that appear in the temperature distributions during quasi-static tensile testing of bioinert alloys. These alloys include VT1-0 titanium, Zr-1%Nb and Ti-45%Nb in both coarse-grain (CG) and ultrafine-grain (UFG) states. The crystal structure, as well as the crystal domain and grain sizes of these alloys in the UFG state, may be different from the CG versions and identifying the thermal signatures that occur during their deformation and fracture is of interest, as it may lead to an understanding of physical processes that occur during loading. By comparing the surface temperature distributions of specimens undergoing deformation under tensile loading to the distributions at maximum temperatures it was found that the observed differences depend on the alloy type, the alloy structural state and the thermal properties of structural defects in the specimen. Macro-defects were found in some specimens of VT1-0 titanium, Zr-1Nb and Ti-45Nb alloys in both the CG and UFG states. The average tensile strength of specimens containing defects was lower than that of specimens with no defects. Infrared thermography documents change in the thermal patterns of specimens as they are deformed under tensile loading and when the load stops changing or the specimen breaks.

Active infrared (IR) thermographic nondestructive testing (NDT) has become a valuable inspection method for composite materials due to its high sensitivity to particular types of defect and high inspection rate. The computer-implemented thermal tomography, based on the analysis of heat diffusion in solids, involves a specialized treatment of the data obtained by means of active IR thermographic NDT, thus allowing for the “slicing” of materials under testing for a few layers where discontinuity-like defects can be underlined on the noise-free background (binary thermal tomograms). The time-domain thermal tomography is based on the fact that, in a one-sided test, temperature “footprints” of deeper defects appear later in regard to shallower defects. The phase-domain tomography can be applied to collected IR data in a direct way, for instance, by using the Fourier transform, but quantification of results is more difficult because the relationships between phase and defect depth depend on experimental parameters, and the corresponding “phase vs. defect depth” calibration functions are ambiguous. In this study, the time- and phase-domain thermal tomography techniques have been compared on simulated IR thermograms and experimentally applied to the evaluation of carbon fiber reinforced plastic composite containing impact damage defects characterized by impact energy 10, 18, and 63 J. Both tomographic techniques have demonstrated similar results in the reconstruction of thermal tomograms and, in some cases, supplied complementary information about the distribution of single defect zones within impacted areas.

Thermal nondestructive testing can be used to inspect reinforced concrete supports that are widely used in various industries. Corrosion damage is a typical defect found in these supports. Corrosion usually starts as a separation between the concrete and the steel rebar. Damage is exacerbated by pressure that is caused by the formation of corrosion products. The most logical method for using IR to detect corrosion or a disbond would be to heat up the rebar by resistive or inductive heating. In both cases, monitoring the dynamic temperature distributions on the pole allows for the evaluation of reinforcement quality. The thermal properties of steel, concrete, air, and corrosion products differ greatly. The magnitude of temperature anomalies and their behavior over time depend on the presence of corrosion products, air gaps, and the quality of contact between rebar and concrete.