Conventional manufacturing of glass microfluidic devices is a complex, multi-step process that involves a combination of different fabrication techniques, typically photolithography, chemical/dry etching and thermal/anodic bonding. As a result, the process is time-consuming and expensive, in particular when developing microfluidic prototypes or even manufacturing them in low quantity. This report describes a fabrication technique in which a picosecond pulsed laser system is the only tool required to manufacture a microfluidic device from transparent glass substrates. The laser system is used for the generation of microfluidic patterns directly on glass, the drilling of inlet/outlet ports in glass covers, and the bonding of two glass plates together in order to enclose the laser-generated patterns from the top. This method enables the manufacturing of a fully-functional microfluidic device in a few hours, without using any projection masks, dangerous chemicals, and additional expensive tools, e.g., a mask writer or bonding machine. The method allows the fabrication of various types of microfluidic devices, e.g., Hele-Shaw cells and microfluidics comprising complex patterns resembling up-scaled cross-sections of realistic rock samples, suitable for the investigation of CO₂ storage, water remediation and hydrocarbon recovery processes. The method also provides a route for embedding small 3D objects inside these devices.

Understanding transport phenomena and governing mechanisms of different physical and chemical processes in porous media has been a critical research area for decades. Correlating fluid flow behaviour at the micro-scale with macro-scale parameters, such as relative permeability and capillary pressure, is key to understanding the processes governing subsurface systems, and this in turn allows us to improve the accuracy of modelling and simulations of transport phenomena at a large scale. Over the last two decades, there have been significant developments in our understanding of pore-scale processes and modelling of complex underground systems. Microfluidic devices (micromodels) and imaging techniques, as facilitators to link experimental observations to simulation, have greatly contributed to these achievements. Although several reviews exist covering separately advances in one of these two areas, we present here a detailed review integrating recent advances and applications in both micromodels and imaging techniques. This includes a comprehensive analysis of critical aspects of fabrication techniques of micromodels, and the most recent advances such as embedding fibre optic sensors in micromodels for research applications. To complete the analysis of visualization techniques, we have thoroughly reviewed the most applicable imaging techniques in the area of geoscience and geo-energy. Moreover, the integration of microfluidic devices and imaging techniques was highlighted as appropriate. In this review, we focus particularly on four prominent yet very wide application areas, namely “fluid flow in porous media”, “flow in heterogeneous rocks and fractures”, “reactive transport, solute and colloid transport”, and finally “porous media characterization”. In summary, this review provides an in-depth analysis of micromodels and imaging techniques that can help to guide future research in the in-situ visualization of fluid flow in porous media.

We investigate the feasibility of cutting and drilling thin flex glass (TFG) substrates using a picosecond laser operating at wavelengths of 1030nm, 515nm and 343nm. 50μm and 100μm thick AF32®Eco Thin Glass (Schott AG) sheets are used. The laser processing parameters such as the wavelength, pulse energy, pulse repetition frequency, scan speed and the number of laser passes which are necessary to perform through a cut or to drill a borehole in the TFG substrate are studied in detail. Our results show that the highest effective cutting speeds (220mm/s for a 50μm thick TFG substrate and 74mm/s for a 100μm thick TFG substrate) are obtained with the 1030nm wavelength, whereas the 343nm wavelength provides the best quality cuts. The 515nm wavelength, meanwhile, can be used to provide relatively good laser cut quality with heat affected zones (HAZ) of <25μm for 50μm TFG and <40μm for 100μm TFG with cutting speeds of 100mm/s and 28.5mm/s, respectively. The 343nm and 515nm wavelengths can also be used for drilling micro-holes (with inlet diameters of ⩽75µm) in the 100μm TFG substrate with speeds of up to 2 holes per second (using 343nm) and 8 holes per second (using 515nm). Optical microscope and SEM images of the cuts and micro-holes are presented

A nanosecond pulsed Nd:YAG fibre laser with wavelength of 1064nm was used to texture several different steels, including grade 304 stainless steel, grade 316 stainless steel, Cr–Mo–Al ‘nitriding’ steel and low alloy carbon steel, in order to generate surfaces with a high static friction coefficient. Such surfaces have applications, for example, in large engines to reduce the tightening forces required for a joint or to secure precision fittings easily. For the generation of high friction textures, a hexagonal arrangement of laser pulses was used with various pulse overlaps and pulse energies. Friction testing of the samples suggests that the pulse energy should be high (around 0.8mJ) and the laser pulse overlap should be higher than 50% in order to achieve a static friction coefficient of more than 0.5. It was also noted that laser processing increases the surface hardness of samples which appears to correlate with the increase in friction. Energy-Dispersive X-ray spectroscopy (EDX) measurements indicate that this hardness is caused by the formation of hard metal-oxides at the material surface

Conventional manufacturing of microfluidic devices from glass substrates is a complex, multi-step process that involves different fabrication techniques and tools. Hence, it is time-consuming and expensive, in particular for the prototyping of microfluidic devices in low quantities. This article describes a laser-based process that enables the rapid manufacturing of enclosed micro-structures by laser micromachining and microwelding of two 1.1-mm-thick borosilicate glass plates. The fabrication process was carried out only with a picosecond laser (Trumpf TruMicro 5×50) that was used for: (a) the generation of microfluidic patterns on glass, (b) the drilling of inlet/outlet ports into the material, and (c) the bonding of two glass plates together in order to enclose the laser-generated microstructures. Using this manufacturing approach, a fully-functional microfluidic device can be fabricated in less than two hours. Initial fluid flow experiments proved that the laser-generated microstructures are completely sealed; thus, they show a potential use in many industrial and scientific areas. This includes geological and petroleum engineering research, where such microfluidic devices can be used to investigate single-phase and multi-phase flow of various fluids (such as brine, oil, and CO₂) in porous media.