Stacked InAs/InGaAs quantum dots are used as an active media of metamorphic InGaAs–InGaAlAs lasers grown on GaAs substrates by molecular beam epitaxy. High quantum efficiency (η_i>60%) and low internal losses (α<3–4 cm⁻¹) are realised. The transparency current density per single QD layer is estimated as ∼70 A/cm² and the characteristic temperature is 60 K (20–85°C). The emission wavelength exceeds 1.51 µm at temperatures above 60°C.

We review epitaxial formation, basic properties, and device applications of a novel type of nanostructures of mixed (0D/2D) dimensionality that we refer to as quantum well-dots (QWDs). QWDs are formed by metalorganic vapor phase epitaxial deposition of 4–16 monolayers of In_xGa_1−xAs of moderate indium composition (0.3 < x < 0.5) on GaAs substrates and represent dense arrays of carrier localizing indium-rich regions inside In-depleted residual quantum wells. QWDs are intermediate in properties between 2D quantum wells and 0D quantum dots and show some advantages of both of those. In particular, they offer high optical gain/absorption coefficients as well as reduced carrier diffusion in the plane of the active region. Edge-emitting QWD lasers demonstrate low internal loss of 0.7 cm⁻¹ and high internal quantum efficiency of 87%. as well as a reasonably high level of continuous wave (CW) power at room temperature. Due to the high optical gain and suppressed non-radiative recombination at processed sidewalls, QWDs are especially advantageous for microlasers. Thirty-one μm in diameter microdisk lasers show a high record for this type of devices output power of 18 mW. The CW lasing is observed up to 110 °C. A maximum 3-dB modulation bandwidth of 6.7 GHz is measured in the 23 μm in diameter microdisks operating uncooled without a heatsink. The open eye diagram is observed up to 12.5 Gbit/s, and error-free 10 Gbit/s data transmission at 30 °C without using an external optical amplifier, and temperature stabilization is demonstrated.

We study injection GaAs-based microdisk lasers capable of operating at room and elevated temperatures. A novel type of active region is used, namely InGaAs quantum well-dots representing a dense array of indium-rich islands formed inside an indium-depleted residual quantum well by metalorganic vapor phase epitaxy. We demonstrate a high output power of 18 mW, a differential efficiency of about 31%, and a peak electrical-to-optical power conversion efficiency of 15% in a 31 μm diameter microdisk laser. The continuous-wave lasing is observed up to 110°C.