We review epitaxial formation, basic properties, and device applications of a novel type of nanostructures of mixed (0D/2D) dimensionality that we refer to as quantum well-dots (QWDs). QWDs are formed by metalorganic vapor phase epitaxial deposition of 4–16 monolayers of In_xGa_1−xAs of moderate indium composition (0.3 < x < 0.5) on GaAs substrates and represent dense arrays of carrier localizing indium-rich regions inside In-depleted residual quantum wells. QWDs are intermediate in properties between 2D quantum wells and 0D quantum dots and show some advantages of both of those. In particular, they offer high optical gain/absorption coefficients as well as reduced carrier diffusion in the plane of the active region. Edge-emitting QWD lasers demonstrate low internal loss of 0.7 cm⁻¹ and high internal quantum efficiency of 87%. as well as a reasonably high level of continuous wave (CW) power at room temperature. Due to the high optical gain and suppressed non-radiative recombination at processed sidewalls, QWDs are especially advantageous for microlasers. Thirty-one μm in diameter microdisk lasers show a high record for this type of devices output power of 18 mW. The CW lasing is observed up to 110 °C. A maximum 3-dB modulation bandwidth of 6.7 GHz is measured in the 23 μm in diameter microdisks operating uncooled without a heatsink. The open eye diagram is observed up to 12.5 Gbit/s, and error-free 10 Gbit/s data transmission at 30 °C without using an external optical amplifier, and temperature stabilization is demonstrated.

We study injection GaAs-based microdisk lasers capable of operating at room and elevated temperatures. A novel type of active region is used, namely InGaAs quantum well-dots representing a dense array of indium-rich islands formed inside an indium-depleted residual quantum well by metalorganic vapor phase epitaxy. We demonstrate a high output power of 18 mW, a differential efficiency of about 31%, and a peak electrical-to-optical power conversion efficiency of 15% in a 31 μm diameter microdisk laser. The continuous-wave lasing is observed up to 110°C.

High-performance injection microdisk (MD) lasers grown on Si substrate are demonstrated for the first time, to the best of our knowledge. Continuous-wave (CW) lasing in microlasers with diameters from 14 to 30 μm is achieved at room temperature. The minimal threshold current density of $600\mathrm{A}/{\mathrm{cm}}^2$ (room temperature, CW regime, heatsink-free uncooled operation) is comparable to that of high-quality MD lasers on GaAs substrates. Microlasers on silicon emit in the wavelength range of 1320–1350 nm via the ground state transition of InAs/InGaAs/GaAs quantum dots. The high stability of the lasing wavelength ($d\lambda /dI=0.1\mathrm{nm}/\mathrm{mA}$) and the low specific thermal resistance of $4\times {10}^{-3}°\mathrm{C}\times {\mathrm{cm}}^2/\mathrm{W}$ are demonstrated.

Ultrasmall microring and microdisk lasers with an asymmetric air/GaAs/Al0.98Ga0.02As waveguide and an active region based on InAs/InGaAs/GaAs quantum dots emitting around 1.3 μm were fabricated and studied. The diameter D of the microrings and microdisks was either 2 or 1.5 μm, and the inner diameter d of the microrings varied from 20% to 70% of the outer diameter D. The microring with D = 2 μm and d = 0.8 μm demonstrated a threshold pump power as low as 1.8 μW at room temperature. Lasing was observed up to 100°C owing to the use of quantum dots providing high confinement energy both for electrons and holes. Tuning spectral positions of the whispering gallery modes via changing the inner diameters of the microrings was demonstrated. 78.67.Hc; 42.55.Sa; 42.50.Pq; 78.55.Cr