The current consumer demand for fresh food and the interest in caring for the environment have driven the development of biodegradable film packaging to replace synthetic films to preserve the integrity of food. The objective of this work was to evaluate the effects of starch modifications (oxidized, cross-linked, and dual: oxidized/cross-linked), starch concentration (1 and 2%), and glycerol concentration (5 and 15%) on water vapor permeability (WVP), mechanical properties (tensile strength and elongation), optical, and structural properties of films based on “hawthorn” yam starch. The WVP of the films was 4.4 × 10−10 to 1.5 × 10−9 g/m∗s∗Pa, where the films with oxidized yam starch showed a 58.04% reduction concerning the native starch. The tensile strength of oxidized yam starch films showed a decrease of 17.51% with an increase in glycerol concentration. For the 1% starch concentration, elongation increased by 17.03% when the glycerol concentration was increased from 5 to 15%. Modification of starch, starch concentration, and glycerol have a significant effect on the barrier, mechanical, physical, and structural properties of films made with yam starch, where films made with oxidized yam starches at a concentration of 1% starch and 5% glycerol showed the best responses of the properties evaluated.

Edible films can be formed from different polymeric compounds. The use of starch has gained extra value; because it can be used in combination with plasticizers and lipids, helping to improve mechanical properties. Besides, with the addition of an antimicrobial, the function of these films can be extended. The objective of this research was to evaluate the effect of native cassava starch, beeswax and ethanolic propolis extract (EPE) on the mechanical, thermal and inhibitory properties against the Aspergillus niger fungus. An experimental Box-Behnken design with three factors: cassava starch concentration (2–4%w/v), beeswax (0.5–0.9%w/w) and EPE (1–4%v/w) was used. The films obtained were opaque and with low mechanical properties. EPE concentration affected tensile strength, elongation at break (EB) and Young’s modulus (YM), and cassava starch content only affected EB and YM. In thermal properties, the weight loss was affected by the cassava starch-beeswax interaction, where the most loss occurred at high levels of these factors in the temperature range of 200–360 °C. The films reduced the growth of the Aspergillus niger by 51%, where the beeswax-EPE interaction had a significant positive effect. The characteristics of the developed films suggest that they would be more acceptable as fruit and vegetable coatings.

Broccoli sprouts are a recognized source of health-promoting compounds, such as glucosinolates, glucoraphanin, and sulforaphane (SFN). Maximization of SFN content can be achieved by technological processing. We investigated the effect of blanching conditions to determine the optimal treatment that maximizes sulforaphane content in broccoli sprouts. Broccoli seeds (cv. Traditional) grown under controlled conditions were harvested after 11 days from germination and subjected to different blanching conditions based on a central composite design with temperature and time as experimental factors. Results were analyzed by ANOVA followed by a Tukey test. The optimum conditions were identified through response surface methodology. Blanching increased sulforaphane content compared with untreated sprouts, agreeing with a decrease in total glucosinolates and glucoraphanin content. Temperature significantly affected SFN content. Higher temperatures and shorter immersion times favor glucoraphanin hydrolysis, thus increasing SFN content. The optimum conditions were blanching at 61 °C for 4.8 min, resulting in 54.3 ± 0.20 µmol SFN/g dry weight, representing a 3.3-fold increase with respect to untreated sprouts. This is the highest SFN content reported for sprouts subjected to any treatment so far. The process described in this work may contribute to developing functional foods and nutraceuticals that provide sulforaphane as an active principle.