The incorporation of waste materials generated in many industries has been actively advocated for in the construction industry, since they have the capacity to lessen the pollution on dumpsites, mitigate environmental resource consumption, and establish a sustainable environment. This research has been conducted to determine the influence of different rice husk ash (RHA) concentrations on the fresh and mechanical properties of high-strength concrete. RHA was employed to partially replace the cement at 5%, 10%, 15%, and 20% by weight. Fresh properties, such as slump, compacting factor, density, and surface absorption, were determined. In contrast, its mechanical properties, such as compressive strength, splitting tensile strength and flexural strength, were assessed after 7, 28, and 60 days. In addition, the microstructural evaluation, initial surface absorption test, = environmental impact, and cost–benefit analysis were evaluated. The results show that the incorporation of RHA reduces the workability of fresh mixes, while enhancing their compressive, splitting, and flexural strength up to 7.16%, 7.03%, and 3.82%, respectively. Moreover, incorporating 10% of RHA provides the highest compressive strength, splitting tensile, and flexural strength, with an improved initial surface absorption and microstructural evaluation and greater eco-strength efficiencies. Finally, a relatively lower CO₂-eq (equivalent to kg CO₂) per MPa for RHA concrete indicates the significant positive impact due to the reduced Global Warming Potential (GWP). Thus, the current findings demonstrated that RHA can be used in the concrete industry as a possible revenue source for developing sustainable concretes with high performance.

This research work is devoted to the experimental investigation of both rheological and mechanical properties of self-compacting concrete (SCC) produced with waste galvanized copper wire fiber and rice husk ash (RHA). In the study, three different volume fractions of 0.5 p to 0.75 percent, 1 percent of scrap copper wire fiber as reinforcing material, and 2 percent RHA as cement replacement were used. To evaluate the fresh characteristics of SCC, the slump flow, J-ring, and V-funnel experiments were conducted for this investigation. Compressive strength, splitting tensile strength, and flexural strength of the concrete were conducted to assess the hardened properties. The test was carried out to compare each characteristic of plain SCC with this modified SCC mixture, containing RHA as pozzolanic materials and copper fiber as reinforcing material. Incorporating copper fiber in the SCC leads to a drop in fresh properties compared to plain SCC but remains within an acceptable range. On the other hand, the inclusion of 2% RHA makes the SCC more viscous. Although adding 2% RHA and 1% copper wire in SCC provide the highest strength, this mix has an unacceptable passing ability. The SCC mix prepared with 2% RHA and 0.75% copper fiber is suggested to be optimum in terms of the overall performance. According to this study, adding metallic fiber reinforcement like copper wire and mineral admixture like RHA can improve the mechanical properties of SCC up to a certain level.

The purpose of this paper is to develop gather data on the rheological and mechanical properties of self-compacting concrete (SCC) containing varying percentages of waste glass aggregate (WGA). In this current experiment, the coarse aggregate was substituted by adding WGA, with replacement percentages of 0%, 10%, 20%, and 30% by weight being investigated. The rheological properties of SCC were performed to explore the consequence of WGA using various methods, including the J-ring, slump flow, L-box, and V-funnel. In contrast, the compressive, flexural, modulus of elasticity, and stress-strain responses of hardened concrete were assessed in this study. The results of the fresh concrete tests revealed that the substitution of an optimal level of waste glass in SCC provides adequate implementation in flowability, passing ability, and viscosity behaviors. Besides, hardened characteristics were shown to have a steady decrease in strength with increasing WGA content in the concrete mixtures.

Implementation of self-consolidating concrete (SCC) leads to the evaluation of more attractive, quality-controlled concrete with improved workability in the construction sector. The aim of the paper involves the determination of the rheological properties of SCC using waste glass aggregate, which affects the concrete’s rheological behaviour. In this research, the conventional coarse aggregate was substituted by the waste glass aggregate (WGA), at 10%, 20% and 30%, respectively. The consequence of adding waste glass in fresh concrete was inspected by several tests such as density, slump flow, J-ring, L-box and V-funnel test. These properties were then compared to the corresponding properties of normal-weight concrete. Test results specify that the WGA amplified the slump value of SCC thus indicates the improved workability. The decreasing density of the SCC leads it to the lightweight concrete. Subsequently, the SCC concrete shows relatively reduction in the passing ability with the addition of waste glass due to the angular shape of the glass bits. Hence, the study concludes that all of the rheological properties of self-compacting glass concrete (SCGC) made of WGA showed an impressing enhancement in the result, in comparison with the conventional SCC.