The hydrogen embrittlement (HE) behavior of a commercial QP980 steel is studied in this work. The HE susceptibility results indicate that QP980 suffers from a severe HE, and the fracture mode transforms from ductile dimpling to brittle quasi-cleavage under the attack of hydrogen. The EBSD results show that strain-induced martensite transformation can rarely occur at a strain close to the HE fracture strain, which is mainly attributed to the high mechanical stability of austenite. The TKD-KAM analysis results indicate that hydrogen-induced strain localization in martensite can be mitigated by the hydrogen-trapping effect of surrounding austenite, while it is most pronounced in martensite adjacent to ferrite. Correspondingly, HE cracking is considered to initiate in martensite adjacent to ferrite under the synergistic action of HELP and HEDE mechanisms, and then cracks can propagate through ferrite or along phase interfaces. Our findings suggest that to further improve the HE resistance of QP steel with stable austenite, it is necessary to consider introducing effective hydrogen-trapping sites (such as carbides, film austenite) into martensite, which is deemed to be beneficial for increasing the resistance against hydrogen-induced cracking initiation in martensite.

Defects would occur in the weld joint of the wheel rims during the post-flash butt welding (FBW) process suffering from poor plasticity, which will deteriorate the quality and lifecycle of finish products. Therefore, the FBW process of the 440CL high-strength-low-alloy (HSLA) steel was physically simulated and the influence of flash parameters on FBW joints was systematically evaluated in this study. The results showed that the width of heat affected zone increased with accumulated flash allowance (δ_f) while declined with accelerated flash speed (v_f). The recrystallization level would be intensified with increased δ_f. Meanwhile, the acceleration in v_f populated the WZ with a more homogeneous microstructure, higher recrystallization degree and lower dislocation density. The hardness in WZ slightly reduced (202 → 195 HV) as increased δ_f but obviously dropped (192 → 177 HV) as increased v_f. All tensile samples were fractured at the BM location and the tensile properties of FBW joints exhibit a good match with those of BM, with a slight increase in strength (UTS: 468 ~ 493 MPa; YS: 370 ~ 403 MPa) but a mild decrease in plasticity (EL: 39 ~ 44%; RA: 74 ~ 79%). Furthermore, both the joint strength and ductility showed a downward tendency with the increment of δ_f. However, the strength slightly decreased while the ductility increased with the advancement of v_f. These findings would be valuably referential to the real FBW of HSLA steels with optimized microstructure and mechanical performance.

In this study, finite element (FE) simulation by the software Abaqus was relied on to investigate the roll forming process of a wheel rim made of an innovative dual-phase steel, i.e., DP590, after flash butt welding (FBW). In the simulation, an FE model was generated, including the design of the dies for flaring, three-roll forming, and expansion, and detailed key processing parameters based on practical production of the selected DP590. Combined with the microstructures and properties of the weld zone (WZ) and heat-affected zones (HAZs) after FBW, the distribution of stress/strain and the change in thickness of the base metal (BM), WZ and HAZs were analyzed, and compared in the important stages of roll forming. Theoretically, the variation in the microstructure and the corresponding stress–strain behaviors of the BM, WZ, and HAZs after FBW have led to the thickness reduction of DP590 that originated from softening behaviors occurring at the region of subcritical HAZs (SCHAZs), and a small amount of tempered martensite has evidently reduced the hardness and strength of the SCHAZ. Meanwhile, the distribution of stress/strain has been influenced to some extent. Further, the study includes the influence of the friction coefficient on the forming quality of the wheel rim to guarantee the simulation accuracy in practical applications. In sum, the dual-phase steel has to be carefully applied to the wheel rim, which needs to experience the processes of FBW and roll forming, focusing on the performance of SCHAZs.