This review paper presents an overview of the state of the art on process-induced degradation of poly(lactic acid) (PLA) and the relative importance of different processing variables. The sensitivity of PLA to degradation, especially during melt processing, is considered a significant challenge as it may result in deterioration of its properties. The focus of this review is on degradation during melt processing techniques such as injection molding and extrusion, and therefore it does not deal with biodegradation. Firstly, the general processing and fundamental variables that determine the degradation are discussed. Secondly, the material properties (for example rheological, thermal, and mechanical) are presented that can be used to monitor and quantify the degradation. Thirdly, the effects of different processing variables on the extent of degradation are reviewed. Fourthly, additives are discussed for melt stabilization of PLA. Although current literature reports the degradation reactions and clearly indicates the effect of degradation on PLA’s properties, there are still knowledge gaps in how to select and predict the processing conditions that minimize process-induced degradation to save raw materials and time during production.

One of the drawbacks of natural fibers and their composites is their inherent hydrophilic nature. The effect of moisture on the mechanical properties of composites is irrefutable. This study deals with the hygroscopic characteristics of enset–PLA composites and their effect on the mechanical properties of the composites. To do this, injection-molded composite specimens with different fiber volume fractions, plasticizer ratios, fiber lengths, and fiber ages were considered. The specimens were exposed to distilled water, and the moisture absorption was monitored on a daily basis. Subsequently, the specimens were subjected to mechanical loading to determine the effect of moisture on their strength, stiffness, and strain at break strength. Lastly, the individual and joint effects of the considered factors were scrutinized using an optimal experimental design. The results of the study show that the maximum and minimum moisture uptakes were recorded for 25% and 15% fiber ratios, respectively. Due to the effect of moisture, the tensile and bending strength decreased by 11% and 5%, respectively, for the 15% fiber volume fraction and decreased by 16% and 13%, respectively, for the 25% fiber volume fraction. Increasing the amount of plasticizer increases the moisture resistance. The results indicate that Enset–PLA composites have competitive properties and stability when exposed to moisture.

The complete flax stem, which contains shives and technical fibres, has the potential to reduce the cost, energy consumption and environmental impacts of the composite production process if used directly as reinforcement in a polymer matrix. Earlier studies have utilised flax stem as reinforcement in non-bio-based and non-biodegradable matrices not completely exploiting the bio-sourced and biodegradable nature of flax. We investigated the potential of using flax stem as reinforcement in a polylactic acid (PLA) matrix to produce a lightweight, fully bio-based composite with improved mechanical properties. Furthermore, we developed a mathematical approach to predict the material stiffness of the full composite part produced by the injection moulding process, considering a three-phase micromechanical model, where the effects of local orientations are accounted. Injection moulded plates with a flax content of up to 20 V% were fabricated to study the effect of flax shives and full straw flax on the mechanical properties of the material. A 62% increase in longitudinal stiffness was obtained, resulting in a 10% higher specific stiffness, compared to a short glass fibre-reinforced reference composite. Moreover, the anisotropy ratio of the flax-reinforced composite was 21% lower, compared to the short glass fibre material. This lower anisotropy ratio is attributed to the presence of the flax shives. Considering the fibre orientation in the injection moulded plates predicted with Moldflow simulations, a high agreement between experimental and predicted stiffness data was obtained. The use of flax stems as polymer reinforcement provides an alternative to the use of short technical fibres that require intensive extraction and purification steps and are known to be cumbersome to feed to the compounder.

In this study, bio-composites were developed using polylactic acid (PLA) as the matrix and sisal fibers (SFs) derived from agave sisalana leaves as the reinforcement. The bio-composites were prepared through injection molding with the addition of tributyl 2-acetylcitrate (ATBC) plasticizer. The mechanical, thermal, and rheological properties of these bio-composites were investigated to understand the effects of fiber and plasticizer contents. The results showed that the addition of SFs improved the tensile and flexural moduli of the bio-composites but led to a decrease in tensile strength compared to neat PLA. The flexural strength initially decreased with low fiber content but recovered to the level of neat PLA as the fiber content increased. The impact strength increased with the incorporation of SFs and ATBC. However, the presence of ATBC had a negative impact on the tensile and flexural properties of the bio-composites. The thermal conductivity of the materials was influenced by the fiber content and processing temperature, increasing with SFs inclusion but decreasing with temperature. Differential scanning calorimetry analysis revealed increased crystallinity of PLA with the presence of SFs and ATBC. The specific heat capacity increased with ATBC but decreased with increasing SFs. Dynamic mechanical property testing showed variations in storage and loss moduli of the bio-composites at different temperatures. The storage modulus increased with higher fiber content and abruptly dropped around glass transition temperature. Rheological characterization demonstrated effective interactions between the fibers and matrix with good fiber dispersion, resulting in uniform shear viscosity versus shear rate for different capillary dimensions. The shear viscosity of the SFs/PLA mixture increased with increasing fiber content but decreased with the addition of plasticizer. Furthermore, the compounding and molding processes had a notable impact on the microstructure of the fibers, specifically resulting in fiber breakage and fiber separation during processing.