The use of natural fibers in cementitious composites continue gaining acceptability and applicability due to the shortcomings and disadvantages of synthetic fiber; this is because natural fibers have advantages of sustainability, eco-friendliness, and economy. Biodegradable natural fibers, being low density and lightweight, with typical values of strength-to-weight ratio, aspect ratio, elastic modulus, and strength, may be competitive for substituting synthetic fibers such as glass and carbon. Indeed, natural fibers are mostly non-irritating for the skin and typically pose no troubles or issues for breathing, which is not the case with many synthetic fibers. Date palm fiber (DPF) is a natural fiber obtained as waste material from a date palm tree. In many countries, with large date production, DPF is easily available as a process by-product, with a low processing cost. Being sustainable and environmentally friendly, DPF is continuously gaining acceptability as fiber material in different composites such as concrete, mortar, gypsum composites, clay composites, and bricks. Based on the most available literature reviewed, DPF reinforced composites have been found to be a good insulation material, with higher thermal properties, thereby reducing energy consumption which consequently saves the running and maintenance cost of the building. DPF reinforced composites were reported to have higher energy absorption capacity, ductility, and bending resistance, leading to delaying crack propagation and preventing catastrophic failures of structures such as beams and slabs. Additionally, due to its lower density, DPF reinforced composites have the advantage for usage in areas prone to seismic effects, and when used for buildings, the overall weight of the building is expected to reduce hence reduction in foundation cost. The major setback of using DPF in composites is the reduction in the compressive strength of the composites and the durability performance of the composites. Therefore, for effective usage of DPF in composites to derive the maximum benefits, there is a need to devise a method of mitigating its negative effects on the compressive strength and durability performance of the Composites; this is a future study that needs to be explored for better performance of DPF in cementitious and other materials composites.

Self-compacting concrete (SCC) was developed to overcome the challenges of concrete placement in dense or congested reinforcement structure, where the concrete can flow under its own weight to fill the densely reinforced structure. However, production of SCC mostly involves the use of high cement to achieve the desired strength. Therefore, to reduce the needed amount of cement, pozzolanic materials such as fly ash can be used to partially replace cement. However, fly ash has been reported to decrease the strengths of concrete especially at early ages. In this study, a self-compacting concrete (SCC) was developed with fly ash as a basic replacement material considering the efficiency of fly ash and incorporating graphene oxide (GO) as a cement additive to counteract the negative effect of fly ash. Response surface methodology (RSM) was utilized for designing the experiments, investigating the effects of fly ash and GO on SCC properties, and developing mathematical models for predicting mechanical properties of SCC. The ranges of fly ash and graphene oxide were 16.67 to 35% and zero to 0.05%, respectively. Statistical analysis was performed by using Design Expert software (version 11.0, Stat Ease Inc., Minneapolis, MS, USA). The results showed that fly ash had a positive effect while GO had a negative effect on the workability of SCC. The incorporation of fly ash alone decreased the compressive strength (CS), splitting tensile strength (STS) and flexural strength (FS), and additionally, increased the porosity of SCC. The addition of GO to fly ash-based SCC reduced its porosity and enhanced its mechanical strengths which was more pronounced at early ages. The developed models for predicting the mechanical strengths of fly ash-based SCC containing GO have a very high degree of correlation. Therefore, the models can predicts the strengths of SCC using fly ash and GO as the variables with a high level of accuracy. The findings show that based on the EFNARC guidelines, up to 35% of fly ash can be used to replace cement in SCC to achieve a mix with satisfactory flowability and deformability properties