Concrete presents different internal micro-structure and damage characteristics because of the different content of steel fibers and the randomness of its distribution. Therefore, the failure process of steel-fiber-reinforced concrete (SFRC) should be divided into different stages and the damage types should be classified to further clarify the strengthening mechanism of steel fibers. The role of volume fractions of steel fibers in the splitting-tensile strength of concrete was investigated by split tensile tests for concrete with four different volume fractions of steel fibers (0.0%, 1.0%, 1.5%, 2.0%). The acoustic emission energy and horizontal displacement of concrete in the splitting-tensile process were monitored by combing digital image correlation (DIC) and acoustic emission (AE) techniques, and the microscopic failure mechanism of SFRC was analyzed emphatically. The results showed that the addition of steel fibers improved the splitting-tensile strength of concrete. With the increase of the volume fraction of steel fibers, the splitting-tensile strength of concrete increased first and then decreased, and reached the maximum value of 5.294 MPa when the content was 1.5%. It was observed that the overall failure mechanism could be divided into four stages: slow accumulation of elastic energy (I); rapid accumulation of elastic energy (II); rapid accumulation of dissipated energy (III); a slow decrease of elastic energy and a slow increase of dissipated energy (IV). Tensile failure dominated the failure process of concrete splitting-tensile resistance, while there was a part of shear failure.

Solid waste silica fume was used to replace fly ash by different ratios to study the early-age hydration reaction and strength formation mechanism of concrete. The change pattern of moisture content in different phases and micro morphological characteristics of concrete at early age were analyzed by low field nuclear magnetic resonance (LF-NMR) and scanning electron microscope (SEM). The results showed that the compressive strength of concrete was enhanced optimally when the replacement ratio of solid waste silica fume was 50%. The results of LF-NMR analysis showed that the water content of modified concrete increased with the increase of solid waste silica fume content. The compressive strength of concrete grew faster within the curing age of 7 d, which means the hydration process of concrete was also faster. The micro morphological characteristics obtained by SEM revealed that the concrete was densest internally when 50% fly ash was replaced by the solid waste silica fume, which was better than the other contents.