A 4:1 (volume ratio) methanol–ethanol (ME) mixture and silicone oil are two of the most widely used liquid pressure-transmitting media (PTM) in high-pressure studies. Their hydrostatic limits have been extensively studied using various methods; however, the evolution of the atomic structures associated with their emerging nonhydrostaticity remains unclear. Here, we monitor their structures as functions of pressure up to ∼30 GPa at room temperature using in situ high-pressure synchrotron x-ray diffraction (XRD), optical micro-Raman spectroscopy, and ruby fluorescence spectroscopy in a diamond anvil cell. No crystallization is observed for either PTM. The pressure dependence of the principal diffraction peak position and width indicates the existence of a glass transition in the 4:1 ME mixture at ∼12 GPa and in the silicone oil at ∼3 GPa, beyond which a pressure gradient emerges and grows quickly with pressure. There may be another liquid-to-liquid transition in the 4:1 ME mixture at ∼5 GPa and two more glass-to-glass transitions in the silicone oil at ∼10 GPa and ∼16 GPa. By contrast, Raman signals only show peak weakening and broadening for typical structural disordering, and Raman spectroscopy seems to be less sensitive than XRD in catching these structural transitions related to hydrostaticity variations in both PTM. These results uncover rich pressure-induced transitions in the two PTM and clarify their effects on hydrostaticity with direct structural evidence. The high-pressure XRD and Raman data on the two PTM obtained in this work could also be helpful in distinguishing between signals from samples and those from PTM in future high-pressure experiments.

Metallic glasses are expected to have quite tunable structures in their configuration space, without the strict constraints of a well-defined crystalline symmetry and large energy barriers separating different states in crystals. However, effectively modulating the structure of metallic glasses is rather difficult. Here, using complementary in situ synchrotron x-ray techniques, we reveal thermal-driven structural ordering in a Ce₆₅Al₁₀Co₂₅ metallic glass, and a reverse disordering process via a pressure-induced rejuvenation between two states with distinct structural order characteristics. Studies on other metallic glass samples with different compositions also show similar phenomena. Our findings demonstrate the feasibility of two-way structural tuning states in terms of their dramatic ordering and disordering far beyond the nearest-neighbor shells with the combination of temperature and pressure, extending accessible states of metallic glasses to unexplored configuration spaces.