Polymorphism, which describes the occurrence of different lattice structures in a crystalline material, is a critical phenomenon in materials science and condensed matter physics. Recently, configuration disorder was compositionally engineered into single lattices, leading to the discovery of high-entropy alloys and high-entropy oxides. For these novel entropy-stabilized forms of crystalline matter with extremely high structural stability, is polymorphism still possible? Here by employing in situ high-pressure synchrotron radiation X-ray diffraction, we reveal a polymorphic transition from face-centred-cubic (fcc) structure to hexagonal-close-packing (hcp) structure in the prototype CoCrFeMnNi high-entropy alloy. The transition is irreversible, and our in situ high-temperature synchrotron radiation X-ray diffraction experiments at different pressures of the retained hcp high-entropy alloy reveal that the fcc phase is a stable polymorph at high temperatures, while the hcp structure is more thermodynamically favourable at lower temperatures. As pressure is increased, the critical temperature for the hcp-to-fcc transformation also rises.

When a material is heated, generally, it dilates. Here, we find a general trend that the average distance between a center atom and atoms in the first nearest-neighbor shell contracts for several metallic melts upon heating. Using synchrotron X-ray diffraction technique and molecular dynamics simulations, we elucidate that this anomaly is caused by the redistribution of polyhedral clusters affected by temperature. In metallic melts, the high-coordinated polyhedra are inclined to evolve into low-coordinated ones with increasing temperature. As the coordination number decreases, the average atomic distance between a center atom and atoms in the first shell of polyhedral clusters is reduced. This phenomenon is a ubiquitous feature for metallic melts consisting of various-sized polyhedra. This finding sheds light on the understanding of atomic structures and thermal behavior of disordered materials and will trigger more experimental and theoretical studies of liquids, amorphous alloys, glasses, and casting temperature effect on solidification process of crystalline materials.

Diamond owes its unique mechanical, thermal, optical, electrical, chemical, and biocompatible materials properties to its complete sp³-carbon network bonding. Crystallinity is another major controlling factor for materials properties. Although other Group-14 elements silicon and germanium have complementary crystalline and amorphous forms consisting of purely sp³ bonds, purely sp³-bonded tetrahedral amorphous carbon has not yet been obtained. In this letter, we combine high pressure and in situ laser heating techniques to convert glassy carbon into “quenchable amorphous diamond”, and recover it to ambient conditions. Our X-ray diffraction, high-resolution transmission electron microscopy and electron energy-loss spectroscopy experiments on the recovered sample and computer simulations confirm its tetrahedral amorphous structure and complete sp³ bonding. This transparent quenchable amorphous diamond has, to our knowledge, the highest density among amorphous carbon materials, and shows incompressibility comparable to crystalline diamond.

To be structural materials, the critical size is always a bottleneck of bulk metallic glasses (BMGs) due to the cooling rate restriction. Here, we report a developed alloy of Zr₄₆Cu_30.14Ag_8.36Al₈Be_7.5, which can be cast into amorphous rods in 73 mm diameter by copper mould casting. The strong glass forming ability of this alloy is closely related to the Be addition, which not only suppresses the phase separation happening in the as-cast Be-free BMG but also sustains low Gibbs free energy difference for crystallization. This finding will stimulate more interests in developing BMGs and their industrial applications.

A 4:1 (volume ratio) methanol–ethanol (ME) mixture and silicone oil are two of the most widely used liquid pressure-transmitting media (PTM) in high-pressure studies. Their hydrostatic limits have been extensively studied using various methods; however, the evolution of the atomic structures associated with their emerging nonhydrostaticity remains unclear. Here, we monitor their structures as functions of pressure up to ∼30 GPa at room temperature using in situ high-pressure synchrotron x-ray diffraction (XRD), optical micro-Raman spectroscopy, and ruby fluorescence spectroscopy in a diamond anvil cell. No crystallization is observed for either PTM. The pressure dependence of the principal diffraction peak position and width indicates the existence of a glass transition in the 4:1 ME mixture at ∼12 GPa and in the silicone oil at ∼3 GPa, beyond which a pressure gradient emerges and grows quickly with pressure. There may be another liquid-to-liquid transition in the 4:1 ME mixture at ∼5 GPa and two more glass-to-glass transitions in the silicone oil at ∼10 GPa and ∼16 GPa. By contrast, Raman signals only show peak weakening and broadening for typical structural disordering, and Raman spectroscopy seems to be less sensitive than XRD in catching these structural transitions related to hydrostaticity variations in both PTM. These results uncover rich pressure-induced transitions in the two PTM and clarify their effects on hydrostaticity with direct structural evidence. The high-pressure XRD and Raman data on the two PTM obtained in this work could also be helpful in distinguishing between signals from samples and those from PTM in future high-pressure experiments.