In this paper, a naturally pressurized gating system has been designed to reduce the turbulence of the melt during casting. The influence of gate dimensions, foam filters, a trident gate and a vortex element were evaluated. Their effect on melt velocity, flow characteristics, number of oxides, casting properties and mechanical properties were observed. ProCAST Simulation software v.2023 and a water flow test were also evaluated to assist in the experimental evaluation of the castings. Melts showed a relationship between melt velocity and porosity of castings. Quantitative evaluation of the surface porosity showed a trend of decreasing porosity with decreasing melt velocity. The greatest reduction in the melt velocity was achieved by a M4 design, which was associated with the highest reduction in the oxides. The pores analyzed proved the presence of oxide layers on their inner surface and a possible theory of pore formation when the initiator of porosity is entrained double oxide layers. The best metal yield was achieved with M1, but the difference between M2 and M4 was negligible (2–5% yield difference), so it can be stated that the beneficial effect of the M4 design in providing the best quality castings is not negated by the increase in metal yield.

The paper deals with the impact of technological parameters on the heat transfer coefficient and microstructure in AlSi12 alloy using squeeze casting technology. The casting with crystallization under pressure was used, specifically direct squeeze casting method. The goal was to affect crystallization by pressure with a value 100 and 150 MPa. The pressure applied to the melt causes a significant increase of the coefficient of heat transfer between the melt and the mold. There is an increase in heat flow by approximately 50% and the heat transfer coefficient of up to 100-fold, depending on the casting conditions. The change in cooling rate influences the morphology of the silicon particles and intermetallic phases. A change of excluded needles to a rod-shaped geometry with significantly shorter length occurs when used gravity casting method. By using the pressure of 150 MPa during the crystallization process, in the structure can be observed an irregular silica particles, but the size does not exceed 25 microns.

The paper deals with the impact of technological parameters on the mechanical properties and microstructure in AlSi12 alloy using squeeze casting technology. The casting with crystallization under pressure was used, specifically direct squeeze casting method. The goal was to affect crystallization by pressure with a value 100 and 150 MPa. From the experiments we can conclude that operating pressure of 100 MPa is sufficient to influence the structural characteristics of the alloy AlSi12. The change in cooling rate influences the morphology of the silicon particles and intermetallic phases. A change of excluded needles to a rod-shaped geometries with significantly shorter length occurs when used gravity casting method. At a pressure of 100 MPa was increased of tensile strength on average of 20%. At a pressure of 150 MPa was increased of tensile strength on average of 30%. During the experiment it was also observed, that increasing difference between the casting temperature and the mold temperature leads to increase of mechanical properties.

Submitted article deals with the methods to improve mould breathability when using the Patternless process method and also examines the influence of opening material grain size on the dimensional and shape precision of made castings. Mentioned...

The paper deals with the impact of technological parameters on the heat transfer coefficient and microstructure in AlCu4Ti alloy using squeeze casting technology. The casting with crystallization under pressure was used, specifically direct squeeze casting method. The goal was to affect crystallization by pressure with a value 100 MPa. The pressure applied to the melt causes a significant increase of the coefficient of heat transfer between the melt and the mold. By rapid cooling the casting was reflected by changes in the structure. On the basis of the measured values of heat flux and heat transfer coefficient were calculated at the interface between the cast and the mold. The observation of microstructure can conclude, there is no significant influencing of the primary phase. As a result of the pressure was reduced porosity.