Intermetallic compounds have been studied for their potential application as structural wear materials or coatings on engineering steels. In the present work, a newly designed intermetallic composite in a Ni–Mo–Si system was fabricated by arc-melting process with commercially pure metal powders as starting materials. The chemical composition of this intermetallic composite is 45Ni–40Mo–15Si (at %), selected according to the ternary alloy diagram. The microstructure was characterized using optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), and energy dispersive spectroscopy (EDS), and the wear-resistant properties at room temperature were evaluated under different wear test conditions. Microstructure characterization showed that the composite has a dense and uniform microstructure. XRD results showed that the intermetallic composite is constituted by a binary intermetallic compound NiMo and a ternary Mo₂Ni₃Si metal silicide phase. Wear test results indicated that the intermetallic composite has an excellent wear-resistance at room-temperature, which is attributed to the high hardness and strong atomic bonding of constituent phases NiMo and Mo₂Ni₃Si.

Intermetallic composite has been expected to be one kind of high-performance wear material at elevated temperature due to its inherent high hardness and strong atomic bonds. This paper presents the wear behaviors under elevated temperature conditions of NiMo/Mo2Ni3Si intermetallic composite. Metallographic observations were carried out with optical microscope and scanning electron microscope. Elevated-temperature wear tests were performed under pin-on-disc mode dry sliding conditions. Results shown that the relative wear resistant property of NiMo/Mo2Ni3Si alloys at 500 C compared with austenitic 1Cr18Ni9Ti stainless steel. The effect of temperature and applied load on elevated-temperature wear resistance of alloy was evaluated. The corresponding wear mechanism is also reported through examining the worn surface, subsurface, and wear debris of the NiMo/Mo2Ni3Si intermetallic alloys which is found to be soft abrasive wear.

Intermetallic compounds are increasingly being expected to be utilized in tribological environments, but to date their implementation is hindered by insufficient ductility at low and medium temperatures. This paper presents a novel multiphase intermetallic alloy with the chemical composition of Mo–40Ni–13Si (at %). Microstructure characterization reveals that a certain amount of ductile Mo phases formed during the solidification process of a ternary Mo–Ni–Si molten alloy, which is beneficial to the improvement of ductility of intermetallic alloys. Tribological properties of the designed alloy—including wear resistance, friction coefficient, and metallic tribological compatibility—were evaluated under dry sliding wear test conditions at room temperature. Results suggest that the multiphase alloy possesses an excellent tribological property, which is attributed to unique microstructural features and thereby a good combination in hardness and ductility. The corresponding wear mechanism is explained by observing the worn surface, subsurface, and wear debris of the alloy, which was found to be soft abrasive wear.

Intermetallic compounds are increasingly being expected to utilize in tribological environments, but to date the works are hindered by insufficient ductility at low and medium temperature. This paper presents a novel multiphase intermetallic alloy with the chemical composition of Mo-40Ni-13Si (at.%). Microstructure characterization reveals that a certain amount of ductile Mo phases formed during the solidification process of ternary Mo-Ni-Si alloy melt, which is undoubtedly beneficial to the ductility improvement of intermetallic alloy. Tribological properties of the designed alloy, including wear resistance, friction coefficient and metallic tribological compatibility, were evaluated under dry sliding wear test conditions at room temperature. Results suggested that the multiphase alloy possesses an excellent property for room-temperature wear applications, which is attributed to the unique microstructural features and thereby good combination in hardness and ductility. The corresponding wear mechanism is also reported by observing the worn surface, subsurface and wear debris of alloy, which to be found is soft abrasive wear.