Brewers’ spent grain (BSG) is the most abundant by-product of the brewing process. BSG is currently disposed of or used as a supplement for animal feed, although it contains significant amounts of bioactive compounds of great interest to the pharmaceutical, cosmetic and food sectors. In this study we investigate the feasibility of using a simple solvent extraction procedure to recover phenolic antioxidants from BSG. Acetone–water and ethanol–water mixtures were used as extraction solvents. Phenolic extracts obtained by treatment of BSG with the two solvent systems were characterized in terms of total phenolics and antioxidant activity. For both systems, the extraction yield was maximum at 60% (v/v) organic solvent concentration. At all solvent compositions, mixtures containing acetone provided higher extraction yields. As suggested by the strong correlation between the antioxidant activity of BSG extracts and their phenolic content, the antioxidant capacity of the extracts can be mainly attributed to polyphenols. Overall, the obtained results strongly support the exploitation of BSG as a source of phenolic antioxidants and the possibility of recovering them by a mild and green extraction process.

The production of silver nanoparticles (Ag-NPs) from bilberry waste (BW) and red currant waste (RCW) extracts was studied. Red fruit extracts were obtained by treating BW and RCW with aqueous ethanol (50% v/v) at 40 °C. The formation of nanoparticles was monitored spectrophotometrically by measuring the intensity of the surface plasmon resonance band (SPR) of silver. The effects of temperature (20–60 °C) and pH (8–12) on the reaction kinetics and on the properties of Ag-NPs were investigated. Characterization by XRD and dynamic light scattering (DLS) techniques showed that Ag-NPs were highly crystalline, with a face-centered cubic structure and a hydrodynamic diameter of 25–65 nm. The zeta potential was in the range of −35.6 to −20.5 mV. Nanoparticles obtained from BW were slightly smaller and more stable than those from RCW. A kinetic analysis by the initial-rate method showed that there was an optimum pH, around 11, for the production of Ag-NPs. Overall, the results obtained suggest that BW and RCW can be advantageously used as a source of reducing and stabilizing agents for the green synthesis of Ag-NPs.

This work investigates the feasibility of using coffee silverskin (CSS), one of the most abundant coffee waste products, as a reinforcing agent in biopolymer-based composites. The effect of using two compatibilizers, a maleinized linseed oil (MLO) and a traditional silane (APTES, (3-aminopropyl)triethoxysilane), on mechanical and thermal behavior of sustainable composites based on a poly(butylene adipate-co-terephthalate/Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) PBAT/PHBV blend filled with coffee silverskin, in both the as-received state and after the extraction of antioxidants, was studied. Thermal (by differential scanning calorimetry), mechanical (by tensile testing), and morphological properties (by scanning electron microscopy) of injection molded biocomposites at three different weight contents (10, 20, and 30 wt %) were considered and discussed as a function of compatibilizer type. The effects of extraction procedure and silane treatment on surface properties of CSS were investigated by infrared spectroscopy. Obtained results confirmed that extracted CSS and silane-treated CSS provided the best combination of resistance properties and ductility, while MLO provided a limited compatibilization effect with CSS, due to the reduced amount of hydroxyl groups on CSS after extraction, suggesting that the effects of silane modification were more significant than the introduction of plasticizing agent.

Large amounts of spent coffee grounds (SCGs) are produced annually worldwide. SCGs contain high levels of phenolics and other bioactive compounds that make them a potential source of reducing and stabilizing agents for the synthesis of metal nanoparticles. This study investigates the use of SCG extracts as a green strategy to produce silver nanoparticles (AgNPs). SCG extracts were obtained using aqueous ethanol as the solvent and then contacted with a silver nitrate solution under the selected conditions. A central composite design coupled with response surface methodology was used to evaluate the effects of solvent composition (C = 30–70% v/v), silver-to-phenolic ratio (R = 3–7 mol/mol), temperature (T = 25–55 °C) and pH (10–12) on the production of AgNPs. Characterization of AgNPs by DLS, TEM and XRD techniques showed that they were highly crystalline with a narrow size distribution. Under optimal reaction conditions, AgNPs with an average size of about 10 nm and a zeta potential of −30.5 to −20.7 mV were obtained. Overall, the results of this study indicate that SCGs are a promising material for the green synthesis of small-sized and stable AgNPs.