A novel, modified polypyrrole/m-phenylediamine (PPy–mPD) composite, decorated with magnetite (Fe₃O₄) nanoparticles, and prepared via an in-situ oxidative polymerisation, was investigated. The PPy–mPD/Fe₃O₄ nanocomposite was employed for the removal of highly toxic oxyanion hexavalent chromium Cr(VI) from an aqueous solution. The structure and successful formation of the PPy–mPD/Fe₃O₄ nanocomposite was confirmed and investigated using various techniques. The presence of Fe₃O₄ was confirmed by high resolution transmission electron microscopy, with an appearance of Fe lattice fringes. The estimation of the saturation magnetisation of the nanocomposite, using a vibrating sample magnetometer, was observed to be 6.6 emu/g. In batch adsorption experiments, PPy–mPD/Fe₃O₄ nanocomposite (25 mg) was able to remove 99.6% of 100 mg/L of Cr(VI) at pH 2 and 25 °C. Adsorption isotherms were investigated at different Cr(VI) concentration (100–600 mg/L) and temperature (15–45 °C). It was deduced that adsorption follows the Langmuir model, with a maximum adsorption capacity of 555.6 mg/g for Cr(VI) removal. Furthermore, isotherm data were used to calculate thermodynamic values for Gibbs free energy, enthalpy change and entropy change, which indicated that Cr(VI) adsorption was spontaneous and endothermic in nature. Adsorption–desorption experiments revealed that the nanocomposite was usable for two consecutive cycles with no significant loss of adsorption capacity. This research demonstrates the application potential for the fascinating properties of PPy–mPD/Fe₃O₄ nanocomposite as a highly efficient adsorbent for the removal of heavy metal ions from industrial wastewater.

A novel composite of poly(3-aminobenzoic acid) (PABA) and a cobalt zeolitic benzimidazolate framework (CoZIF) has been studied for the production of hydrogen through the hydrogen evolution reaction (HER). The structural characteristics and successful synthesis of PABA, CoZIF and the PABA/CoZIF composite were confirmed and investigated using different techniques. Probing-ray diffraction for phase analysis revealed that the composite showed a decrease and shift in peak intensities, confirming the incorporation of CoZIF on the PABA backbone via in situ polymerization, with an improvement in the crystalline phase of the polymer. The thermal stability of PABA was enhanced upon composite formation. Both scanning electron microscopy and transmission electron microscopy showed that the composite had a rough surface, owing to an interaction between the CoZIF and the external surface of the PABA. The electrochemical hydrogen evolution reaction (HER) performance of the synthesized samples was evaluated using cyclic voltammetry and Tafel analysis. The composite possessed a Tafel slope value of 156 mV/dec and an α of 0.38, suggesting that the Volmer reaction coupled with either the Heyrovsky or Tafel reaction as the rate determining step. The fabricated composite showed high thermal stability and excellent tolerance as well as high electroactivity towards the HER, showing it to be a promising non-noble electrocatalyst to replace Pt-based catalysts for hydrogen generation.

With growth in civilisation and industrialisation, there is an increase in the release of toxic heavy metal ions and dyes into water system, which is of public concern. As a result, appropriate treatment methods have to be implemented in order to mitigate and prevent water pollution. The discovery of nanotechnology has led to the development and utilisation of various nanoadsorbent for the removal of pollutants from water. PANI nanostructures and nanocomposites are noble adsorbents that have gained popularity in addressing water pollution issues and have been reported in literature. In this chapter, the main focus is on the synthesis of PANI nanocomposites and nanostructures and their application as efficient adsorbents for water treatment. Detailed discussions on different synthetic routes and characterisation have been dedicated to applications of these materials and are compared for the adsorptive removal of heavy metal ions and dyes from water.