The development and application of nondestructive testing technology for prestressed reinforced concrete structures in the field of infrastructure construction were summarized in this study via the analysis of relevant literature worldwide. The detection methods, detection principles, and detection instruments in quality evaluation of prestressed reinforced concrete structures were analyzed and compared, based on which, acoustic emission detection technology, impact echo detection technology, ultrasonic detection technology, infrared thermography detection technology, ground-penetrating radar detection technology, piezoelectric transducer detection technology, and X-ray detection technology were summarized. Additionally, the advantages, disadvantages, and application scope of each detection method were focused upon and analyzed comparatively. It is indicated that further improvement in the detection visualization, accuracy, and efficiency for most nondestructive testing technologies is available by optimizing the algorithm and combining artificial intelligence technology with neural network deep learning, precise positioning, and imaging analysis of the quality defects in prestressed reinforced concrete structures. The results of this study can provide technical reference for the further application and research of nondestructive testing technologies in the quality inspection of prestressed reinforced concrete structures.

Recycled aggregate concrete (RAC) is a kind of five-phase composite material at the meso-level. It has a more complex interfacial transition zone (ITZ) than ordinary aggregate concrete (NAC), which is an important factor affecting the meso-failure of RAC. In addition, the maximum aggregate size plays an important role in the nonlinear mechanical behavior of concrete, which is closely related to the size effect. In this paper, a 2D random aggregate model of RAC is established based on meso-mechanics. The mechanical properties and failure modes of RAC under uniaxial compression are simulated using a plastic damage constitutive model. Through variable parameter analysis, the effects of the properties and thickness of ITZ on the elastic modulus and peak stress of RAC are studied, and the effect of the maximum aggregate size on the size effect of the compressive strength of RAC is discussed. The results show that the ITZ strength has a positive linear correlation with the peak stress and elastic modulus of RAC, while the ITZ thickness has a negative linear correlation with the peak stress and elastic modulus of RAC. Under the same specimen size (D = 100 mm, 150 mm, 200 mm, 300 mm), with an increase in the maximum aggregate size (d_max =20 mm, 25 mm, 30 mm, 35 mm), the nominal compressive strength of RAC increases by 6–10%, and the size effect is gradually weakened. When the maximum aggregate size reaches 30 mm, a decrease in the size effect tends to slow down compared with the maximum aggregate size of 20 mm. The classical Bažant size effect law is applicable to describe the compressive properties of RAC under different maximum aggregate sizes, and has a certain guiding significance for the prediction of the size effect of RAC in practical engineering.

The strength-formation mechanism for industrial-construction residue cement stabilization of crushed aggregate (IRCSCA) is not clear. To expand the application range for recycled micro-powders in road engineering, the dosages of eco-friendly hybrid recycled powders (HRPs) with different proportions of RBP and RCP affecting the strengths of cement-fly ash mortar at different ages, and the strength-formation mechanism, were studied with X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results showed that the early strength of the mortar was 2.62 times higher than that of the reference specimen when a 3/2 mass ratio of brick powder and concrete powder was mixed to form the HRP and replace some of the cement. With increasing HRP content substituted for fly ash, the strength of the cement mortar first increased and then decreased. When the HRP content was 35%, the compressive strength of the mortar was 1.56 times higher than that of the reference specimen, and the flexural strength was 1.51 times higher; XRD and SEM studies of the hydrated cement mixed with HRP showed that the amount of CH in the cement paste was reduced by the pozzolanic reaction of HRP at later hydration ages, and it was very useful in improving the compactness of the mortar. The XRD spectrum of the cement paste made with HRP indicated that the CH crystal plane orientation index R, with a diffraction angle peak of approximately 34.0, was consistent with the cement slurry strength evolution law, and this research provides a reference for the application of HRP to produce IRCSCA.