Active and stable catalysts are essential for effective hydrogenation of gaseous CO₂ into valuable chemicals. This work focuses on the structural and catalytic features of single metals, i.e., Co and Ni, as well as bimetallic CoNi alloy catalysts synthesized via combustion of reactive sol-gels. Different characterization methods were used for studying the relationships between the structure, composition, and catalytic activity of the fabricated materials. All catalysts exhibited highly porous sponge-like microstructure. The outermost surfaces of the CoNi alloys were more saturated with Co, while a stoichiometric Co/Ni ratio was observed for the particle’s bulk. Catalytic properties of the as-synthesized powders were studied in the CO₂ hydrogenation reaction at 300 °C for over 80 h of time on stream. All the catalysts demonstrated exceptional selectivity with respect to CH₄ formation. However, the combination of elemental Co and Ni in a single phase resulted in a synergistic effect in bulk alloy catalysts, with activity twofold to threefold that of single-metal catalysts. The activity and stability of the CoNi₃ catalyst were higher than those previously reported for Ni-based catalysts. The reasons for this behavior are discussed.

The bulk of the LiNa₅Mo₉O₃₀ (LNM) crystals were successfully grown in the [010] and [001] directions without internal inclusions and cracks, using the Czochralski method with a low temperature gradient. The crystal grown in the [010] direction showed a tendency to twinning. The crystal grown in the [001] direction demonstrated high structural perfection (FWHM = 13″) for the (001) plane and high optical quality Δn ≈ 2 × 10⁻⁵. The laser-induced damage threshold was measured along a, b and c axes and was 12.2, 27.0 and 27.5 J/cm², respectively. The thermo-optical coefficient dn/dT was measured for the main crystallographic axes, which was −5.75 × 10⁻⁶, −20.2 × 10⁻⁶ and 3.65 × 10⁻⁶ K⁻¹ along the a, b and c axes, respectively. The second harmonic generation (SHG) was conducted in the crystalline LNM sample. The maximum efficiency value of 3.5% at a pump power of 12 W was achieved.

The bulk LiNa5Mo9O30 (LNM) crystals were successfully grown in the [010] and [001] directions without internal inclusions and cracks by the Czochralskii method with low temperature gradient. The crystal grown in the [010] direction showed a tendency to twinning. The crystal grown in the [001] direction demonstrated high structural perfection (FWHM=13'') for the (001) plane and high optical quality Δn≈210-5. The laser induced damage threshold was measured along a, b and c axes and was 15.7, 27.0 and 27.5 J/cm2 respectively. The thermo-optical coefficient dn/dT was measured for the main crystallographic axes, which was -5.7510-6, -2.0210-5 and 3.6510-6 K-1 along the a, b and c axes, respectively. The second harmonic generation (SHG) is conducted in crystalline LNM sample. The maximum efficiency value of 3.5% at pump power of 12 W had been achieved.