Candle light-style OLEDs based on new D–A–π–A type molecules incorporated into Alq₃ matrix were developed. A record low color temperature of 1722 K OLED radiation was achieved, which is by 80 K lower than that of the best devices reported previously.

New oxychloride lead borate glasses in the xPbCl₂–(50-0.5x)PbO–(50-0.5x)B₂O₃ system were synthesized with a maximum lead chloride content of 40 mol%. The characteristic temperatures and mechanical and optical properties were studied. The incorporation of lead chloride led to a significant expansion of the transparency range in the UV (up to 355 nm) and IR regions (up to 4710 nm). Decreases in the Vickers hardness, density, and glass transition temperature were the consequences of a change in the structure. The studied glasses are promising materials for photonics and IR optics. The structure of the PbCl₂–PbO–B₂O₃ system was analyzed in detail using vibrational spectroscopy and X-ray diffraction.