Silver nanowires (AgNWs) show promise for fabricating flexible transparent conductors owing to their excellent conductivity, high transparency, and good mechanical properties. Here, we present the fabrication of transparent films composed of AgNWs with diameters of 20–30 nm and lengths of 25–30 μm on polyethylene terephthalate substrates and glass slides substrates using the Meyer rod method. We systematically investigated the films’ optoelectronic and electrothermal properties. The morphology remained intact when heated at 25–150 °C and the AgNWs film showed high conductivity (17.6–14.3 Ω∙sq⁻¹), excellent transmittance (93.9–91.8%) and low surface roughness values (11.2–14.7 nm). When used as a heater, the transparent AgNW conductive film showed rapid heating at low input voltages owing to a uniform heat distribution across the whole substrate surface. Additionally, the conductivity of the film decreased with increasing bending cycle numbers; however, the film still exhibited a good conductivity and heating performances after repeated bending.

Cu₂ZnSnS₄ (CZTS) is a promising candidate material for photovoltaic applications; hence, ecofriendly methods are required to fabricate CZTS films. In this work, we fabricated CZTS nanocrystal inks by a wet ball milling method, with the use of only nontoxic solvents, followed by filtration. We performed centrifugation to screen the as-milled CZTS and obtain nanocrystals. The distribution of CZTS nanoparticles during centrifugation was examined and nanocrystal inks were obtained after the final centrifugal treatment. The as-fabricated CZTS nanocrystal inks were used to deposit CZTS precursors with precisely controlled CZTS films by a spin-coating method followed by a rapid high pressure sulfur annealing method. Both the grain growth and crystallinity of the CZTS films were promoted and the composition was adjusted from S poor to S-rich by the annealing. XRD and Raman characterization showed no secondary phases in the annealed film, the absence of the detrimental phases. A solar cell efficiency of 6.2% (open circuit voltage: V_oc = 633.3 mV, short circuit current: J_sc = 17.6 mA/cm², and fill factor: FF = 55.8%) with an area of 0.2 cm² was achieved based on the annealed CZTS film as the absorber layer.

Carbon coating has been a routine strategy for improving the performance of Si-based anode materials for lithium-ion batteries. The ability to tailor the thickness, homogeneity and graphitization degree of carbon-coating layers is essential for addressing issues that hamper the real applications of Si anodes. Herein, we report the construction of two-dimensional (2D) assemblies of interconnected Si@graphitic carbon yolk-shell nanoparticles (2D-Si@gC) from commercial Si powders by exploiting oleic acid (OA). The OA molecules act as both the surface-coating ligands for facilitating 2D nanoparticle assembly and the precursor for forming uniform and conformal graphitic shells as thin as 4 nm. The as-prepared 2D-Si@gC with rationally designed void space exhibits excellent rate capability and cycling stability when used as anode materials for lithium-ion batteries, delivering a capacity of 1,150 mAh·g⁻¹ at an ultrahigh current density of 10 A·g⁻¹ and maintaining a stabilized capacity of 1,275 mAh·g⁻¹ after 200 cycles at 4 A·g⁻¹. The formation of yolk-shell nanoparticles confines the deposition of solid electrolyte interphase (SEI) onto the outer carbon shell, while simultaneously providing sufficient space for volumetric expansion of Si nanoparticles. These attributes effectively mitigate the thickness variations of the entire electrode during repeated lithiation and delithiation, which combined with the unique 2D architecture and interconnected graphitic carbon shells of 2D-Si@gC contributes to its superior rate capability and cycling performance. Open image in new window

Flexible transparent conductive films (FTCFs) composed of silver nanowires (AgNWs) have become an important research direction because of their potential in flexible electronic devices. The optoelectronic properties of FTCFs composed of AgNWs of different lengths were evaluated in this study. AgNWs, with an average diameter of about 25 nm and length of 15.49–3.92 μm were obtained by a sonication-induced scission process. AgNW-FTCFs were prepared on polyethylene terephthalate substrates using a Meyer bar and then dried in the ambient environment. The sheet resistance, non-uniformity factor of the sheet resistance, the root mean square roughness, and haze of the FTCFs increased as the length of AgNWs decreased. The transmittance of the films increased slightly as the length of AgNWs increased. AgNWs with a length of 15.49 μm provided an AgNW-FTCF with excellent properties including haze of 0.95%, transmittance of 93.42%, and sheet resistance of 80.15 Ω∙sq⁻¹, without any additional post-treatment of the film. This work investigating the dependence of the optoelectronic properties of AgNW-FTCFs on AgNW length provides design guidelines for development of AgNW-FTCFs.