Studies on field emission (FE) from thin films of zinc oxide (ZnO) nanowires found that both the turn-on voltage and emission current density depend on the areal density of nanowires. The density of ZnO nanowires is controlled by the gold (Au) nanoparticle density deposited on the silicon substrates. The growth of ZnO nanowires was achieved by the thermal evaporation/condensation method. It is shown that the same screening effect observed on carbon nanotube field emitters also affects the FE from thin films of ZnO nanowires. Thin films with the lowest areal density of ZnO nanowires showed much better FE characteristics, comparable to that of carbon nanotubes. More importantly, the FE characteristics of ZnO nanowire thin film were further improved with annealing in hydrogen.

Three-dimensional (3D) printing of silica glass is dominated by techniques that rely on traditional particle sintering. At the nanoscale, this limits their adoption within microsystem technology, which prevents technological breakthroughs. We introduce the sinterless, two-photon polymerization 3D printing of free-form fused silica nanostructures from a polyhedral oligomeric silsesquioxane (POSS) resin. Contrary to particle-loaded sacrificial binders, our POSS resin itself constitutes a continuous silicon-oxygen molecular network that forms transparent fused silica at only 650°C. This temperature is 500°C lower than the sintering temperatures for fusing discrete silica particles to a continuum, which brings silica 3D printing below the melting points of essential microsystem materials. Simultaneously, we achieve a fourfold resolution enhancement, which enables visible light nanophotonics. By demonstrating excellent optical quality, mechanical resilience, ease of processing, and coverable size scale, our material sets a benchmark for micro– and nano–3D printing of inorganic solids.

We describe an acrylic-based prepolymer resin that is ideally suited for the fabrication of three-dimensional structures with two-photon polymerization. We characterize the photochemical and photophysical properties of the photoinitiator and present representative structures that demonstrate the favorable mechanical and optical properties of the polymer.