Photoblinking and photobleaching are commonly encountered problems for single-photon sources. Numerous methods have been devised to suppress these two impediments; however, either the preparation procedures or the operating conditions are relatively harsh, making them difficult to apply to practical applications. Here, we reported giant suppression of both photoblinking and photobleaching of a single fluorescent molecule, terrylene, via the utilization of hexagonal boron nitride (h-BN) flakes as substrates. Experimentally, a much-prolonged survival time of terrylene has been determined, which can have a photostable emission over 2 h at room temperature under ambient atmospheres. Compared with single molecules on a SiO₂/Si substrate or glass coverslip, a more than 100-fold increase in the total number of photons collected from each terrylene on h-BN flakes has been demonstrated. We also proved that the photostability of terrylene molecules can be well maintained for more than 6 months even under ambient conditions without any further protection. Our results demonstrate that the utilization of h-BN flakes to suppress photoblinking and photobleaching of fluorescent molecules has promising applications in the production of high-quality single-photon sources at room temperature.

The achievement of size uniformity and monodispersity in perovskite quantum dots (QDs) requires the implementation of precise temperature control and the establishment of optimal reaction conditions. Nevertheless, the accurate control of a range of reaction variables represents a considerable challenge. This study addresses the aforementioned challenge by employing manganese (Mn) doping to achieve size uniformity in CsPbBr₃ perovskite QDs without the necessity for the precise control of the reaction conditions. By optimizing the Mn:Pb ratio, it is possible to successfully dope CsPbBr₃ QDs with the appropriate concentrations of Mn²⁺ and achieve a uniform size distribution. The spectroscopic measurements on single QDs indicate that the appropriate Mn²⁺ concentrations can result in a narrower spectral linewidth, a longer photoluminescence (PL) lifetime, and a reduced biexciton Auger recombination rate, thus positively affecting the PL properties. This study not only simplifies the size control of perovskite QDs but also demonstrates the potential of Mn-doped CsPbBr₃ QDs for narrow-linewidth light-emitting diode applications.