The design of particle size and morphology are a promising approach to investigating the properties exhibited by different types of materials. In the present study, the silver phosphate microcrystals (Ag₃PO₄) were first time synthesized using the hydrothermal and solvothermal method by combination of the solvents water/isopropyl alcohol (SP-IA), water/acetone (SP-AC), water/ammonium hydroxide (AP-AH), all in a ratio of 1:1 (v/v). The synthesized materials were structurally characterized by X-ray diffraction (XRD), Rietveld refinement, and Raman vibrational spectroscopy, where it was confirmed that the pure phase was achieved for all prepared samples. The study of the optical properties by UV-vis diffuse reflectance spectroscopy (UV-vis/DRS) and colorimetry revealed that the obtained materials have an optical bandgap between 2.30 and 2.32 eV. The FE-SEM images collected revealed different morphologies for the synthesized materials, with a predominance of tetraploid-shaped microcrystals for the SP-AC sample, rods for the SP-IA sample, cubes and polyhedral for the SP-WT sample and condensed polyhedral for the SP-AH sample. The photocatalytic performance against the Rhodamine B dye (RhB) was 100%, 98.2%, 94.2%, and 87.8%, using the samples SP-AC, SP-IA, SP-WT, and SP-AH as photocatalyst at time of 12 min. On the other hand, the antimicrobial performance of SP-AC sample showed superior performance, resulting in the minimum inhibitory concentration-MIC of 7.81 μg mL^-1 for the strain of E. coli, 7.81 μg mL^-1 for the strain of E. aureus, 15.62 μg mL^-1 for the strain of P. auruginosa, and 15.62 μg mL^-1 for the strains of C. albicans. In this way, was synthesized a promissory antimicrobial and photocatalyst material, through an easy and cost-effective method.

This paper reports easy and fast synthesis of PbMoO₄ nanocrystals by microwave-assisted hydrothermal (MH) method at different synthesis times (1, 10, 30 and 60 min) at 100 °C. X-ray diffraction, Rietveld refinement and Raman spectroscopy confirm all characteristics of diffraction peaks and active vibrational modes of the pure scheelite structure (tetragonal, I41/a) for all synthesized PbMoO₄ nanocrystals. The optical bandgap calculated directly from the samples is close to 3.5 eV. The images collected by scanning electron microscopy show particles with mean length from 159.90(8) nm to 303.02(3) nm with greater exposure of planes (111), (100), (011) and (110). The photocatalytic activity of PbMoO₄ nanocrystals against RhB and RBBR dyes resulted in successful degradation in short time intervals using ultraviolet light, where the best performance was achieved for the PbMoO₄-10 sample, which was 29.2 and 51.8 times more effective than photolysis. The contribution of oxidant species was monitored by radical scavengers, which confirms that holes (h⁺) are the main oxidative species in photodegradation of RhB and RBBR dyes, while reuse of the catalyst against RhB and RBBR dyes confirms high stability of the catalyst, although recycled four times.