Today, an important part of paved surfaces in the world uses asphalt mixtures. This practice increases the use of aggregates and fossil fuels, the availability of which is limited. Most of the studies referring to asphalt mixtures reported and compared the mechanical performances without detailing the environmental impacts of the different technologies proposed. The objective of this study was to present and compare through a life cycle assessment using a “cradle-to-gate” approach of different types of asphalt mixtures designed for the same performance, hot mix asphalt (HMA) as a control sample, and warm mix asphalt (WMA) using natural zeolite, Evotherm^® and reclaimed asphalt material (RAP) in different proportions. The analysis was performed using SimaPro 9 software, using the ReCiPe method version 1.11. For the comparison of the environmental impacts, 1 ton of asphalt mixture was used as a functional unit. The most relevant results show that the use of natural zeolite or Evotherm^® helps to reduce environmental impacts. In the global warming impact category, the decrease between the standard HMA and a mix with RAP and natural zeolite was 8%, while in the fossil fuel depletion, the decrease was 13%.

The purpose of this study was to verify the feasibility of using biochar from oat hulls (BO) as a potential bio-modifier to improve the physical properties of conventional asphalt binder. The BO and asphalt binder were characterized by confocal (fluorescence) laser microscopy, scanning electron microscopy and Fourier transform infrared spectroscopy. Then, an asphalt binder modification procedure was established and modifications with 2.5, 5.0 and 7.5% of BO on the weight of the asphalt binder were evaluated, using a particle size < 75 µm. The physical properties of the evaluated modified asphalt binder with BO were: rotational viscosity in original and aged state, aging index, Fraass breaking point, softening point, penetration, penetration rate and storage stability. The results indicated that the BO has a porous structure, able to interact with the asphalt binder by C=O and C=C bonds. In addition, modification of the asphalt binder with BO increases the rotational viscosity related to high-temperature rutting resistance. The results obtained from the Fraass breaking point and softening point indicated that the use of BO extends the viscoelastic range of the asphalt binder. In addition, the evaluated modifications present low susceptibility to aging and good storage stability.

In this study, the effect of biochar from oat hulls (BO) on the rheological properties of a PG 64-22 asphalt binder was evaluated using a full factorial design, which included the following factors: pyrolysis temperature (PT) (300 °C and 500 °C), BO particle size (<20 µm and <75 µm), and the amount of BO (2.5%, 5%, and 7.5%). First, the morphological and physicochemical properties of BO were analyzed by comparing it with graphite powder (CFG) and commercial activated carbon (CAC). The physicochemical properties of the modified asphalt binder were then evaluated using confocal laser microscopy, scanning electron microscopy (SEM–EDX), and Fourier-transform infrared spectroscopy (FTIR). Its storage stability was also evaluated. Subsequently, the rutting parameter G*/sin(δ) and the Fraass breaking point were analyzed to select asphalt binders that extended their viscoelastic range. The asphalt binders selected were those with 2.5%, 5%, and 7.5% BO, produced at a PT of 300 °C with a particle size <20 µm (BO300S). Next, the rheological properties of the selected samples were evaluated by testing for rotational viscosity, rutting parameter G*/sin(δ), multiple stress creep recovery (MSCR), fatigue parameter G*·sin(δ), and creep stiffness by bending beam rheometry (BBR). The rheological aging index according to rutting parameter G*/sin(δ) (RAI) was also evaluated. These tests were conducted in different states of the asphalt binder: original, short-term aged, and long-term aged. According to the results, the application of BO300S significantly increased the resistance of the asphalt binder to rutting and rotational viscosity, proportional to the amount added to the asphalt binder. Moreover, low modifier percentages improved fatigue resistance, outperforming CFG and CAC. In addition, it performs well at low service temperatures, registering better resistance than the control asphalt binders.

Several authors have demonstrated improvements in the mechanical performance of asphalt mixes by including the use of fibers. However, it has also been reported that environmental assessments must address fiber use in asphalt mixes from the point of view of sustainability. In this study, a life cycle assessment is used to compare the use of four different fibers (fiberglass, polyester fiber, aramid fiber, and cellulose fiber) commonly used in hot mix asphalt (HMA) and stone mastic asphalt (SMA) mixes. Additionally, the use of textile fibers from end-of-life tires (FiTyre) is included in the comparison. The results show that in the five selected impact categories (climate change, terrestrial acidification, human toxicity, particulate matter emissions, and the exhaustion of nonrenewable fossil fuels), the use of FiTyre and cellulose fibers is more advantageous than existing traditional fibers (fiberglass, polyester fiber, and aramid fiber).