The purpose of the present work was to study the corrosion behavior of steel coated with epoxy-(organo) clay nanocomposite films. The investigation was carried out using salt spray exposures, optical and scanning electron microscopy examination, open circuit potential, and electrochemical impedance measurements. The mechanical, thermomechanical, and barrier properties of pristine glassy epoxy polymer and epoxy-clay nanocomposites were examined. The degree of intercalation/exfoliation of clay nanoplatelets within the epoxy polymer also was determined. The mechanical, thermomechanical, and barrier properties of all the epoxy-clay nanocomposites were improved compared to those of the pristine epoxy polymer. In addition, both the pristine epoxy and the epoxy nanocomposite coatings protected the steel from corrosion. Furthermore, the protective properties of the nanocomposite coatings were superior compared to those of the pristine epoxy polymer. The protective properties of the nanocomposite coatings varied with the modified clay used. The epoxy-montmorillonite clay modified with primary octadecylammonium ions, Nanomer I.30E, had a better behavior than that modified with quaternary octadecylammonium ions, Nanomer I.28E.

Silane-based materials are used for the protection of heritage and modern buildings. A versatile method is developed to tune the wetting properties of a typical silane-based material from hydrophobicity to superamphiphobicity, thus enhancing the protective efficacy against rainwater and organic pollutants. A commercially available silane product is blended with a fluoropolymer to lower the surface energy and silica (SiO₂) nanoparticles to affect the surface morphologies of the produced coatings on marble. Contact angles of water and oil drops are measured on the coating surfaces which were prepared using 16 different combinations of fluoropolymer and nanoparticle concentrations. It is shown that the synergistic effect of surface structure and chemistry can lead to the production of coatings that possess superamphiphobic properties. The wetting properties of a selected non-wettable coating are further characterised using a custom-made, fully-automated device (Kerberos) which monitors simultaneously the deformation of the liquid interface, spreading and sliding of the drop along the sample surface during tilting. Several tests are carried out to evaluate the durability of the selected superamphiphobic coating, offering overall promising results. The versatile method can be used to impart superamphiphobicity to the surfaces of various materials. The method developed herein can be adopted to tune the wetting properties of other silane-based commercial products which are used for the protection of buildings.

The goal of the study was to characterize the limestone that was used extensively in the ancient city of Pella (Macedonia, Greece), the birthplace of Alexander the Great. An on-site examination of the building material was carried out to record the types of damage and to select sampling areas. A variation in the nature of the stone and the degree of deterioration, even between the stones that comprise a specific monument structure, was observed, with water absorption and biological colonization being the main factors resulting in the deterioration of the stone. A comprehensive microanalysis and testing scheme was conducted to fully characterize the mineralogical, chemical, mechanical and thermal properties of the stones collected from various areas of the archaeological site. Optical microscopy, XRD and SEM–EDX were used to investigate the chemical composition and the structure of the stone samples. Finally, other properties, such as porosity, specific gravity and water absorption, were measured. Surface alterations, material degradation and biological deterioration were observed in most samples. The results obtained using XRD showed that the dominant mineral phase of the limestone is calcite, with quartz and clay minerals also detected in traces. The microscopic examination of the samples showed that the main natural stone at the archaeological site is a marly limestone. Thermographical measurements showed that the decay of the stones due to ambient temperature variation and corresponding contraction/expansion phenomena may be relatively limited, as the stone exhibited a low thermal diffusivity. Moreover, high porosity values (12.06–21.09%) and low compressive strength (11.3–27.7 MPa) were recorded, indicating the vulnerability of the stone and the need to take conservation measures.

Wood, a vital material for both modern and heritage objects, is particularly susceptible to degradation caused by water due to its hydrophilic nature and porous structure. Therefore, developing sustainable strategies to protect wood is of significant importance. This study aims to produce a highly hydrophobic coating for the protection of wood following a straightforward procedure and using materials that are compatible with wood. First, nano/sub-microlignin (NL) is isolated and produced from beech wood through a one-step tailored organosolv process. Next, NL is incorporated into Sivo 121, a water-borne and solvent-free silane system recommended by the manufacturer for protecting wood surfaces. Composite coatings containing various concentrations of NL and Sivo 121 are applied to chestnut (Castanea spp.) and oak (Quercus spp.). The impact of NL concentration on the contact angles of water drops (CAs) and colour changes (ΔE) of the treated wood specimens is investigated. The coating with 4% w/w NL demonstrates enhanced hydrophobicity (CA = 145°) and has a negligible effect on the colour of pristine oak (ΔE < 3). The wetting properties of coated oak are not affected after 100 tape peeling cycles. However, the coating exhibits poorer performance on chestnut, i.e., CA = 135°, which declines after 80 peeling cycles, and ΔE > 5. The drop pH does not have any noticeable effect on CA. The latter remains stable even after prolonged exposure of coated oak and chestnut samples to artificial UV radiation and outdoor environmental conditions. Finally, the composite coating offers good and comparable protection for both wood species in the biological durability soil burial test