This article aims to evaluate the influence of remelting on the experimental Al-Si-Cu type alloy with higher iron content on mechanical properties in relation to the resulting structure. The remelting or recycling process is one of the means of reducing the production costs of the forge plant. The experimental part deals with the analysis of the results of mechanical properties, structural analysis, and the process of crystallization of structural components and their changes due to the increased iron content caused by remelting at different states of the examined alloy. The effect of remelting and ageing on microstructure was observed using a combination of different analytical techniques (light microscopy, scanning electron microscopy (SEM), and upon deep etching and energy dispersive X-ray analysis (EDX)). Tensile strength and elongation tests point to the negative effect of alloying, a gradual increase in wt% Fe and a change in the morphology of the iron phases, which began to manifest significantly after the fourth remelting. The process of natural ageing has been shown to be effective only on alloys with a lower number of remelting cycles, whereas the application of artificial ageing has resulted in improved mechanical properties in all the test alloys.

Iron is the most common and harmful impurity in aluminum casting alloys and has long been associated with an increase of casting defects. While the negative effect of iron is clear, itsmechanism is not fully understood. In generally,iron is as...

The hypoeutectic aluminum alloy AlSi5Cu2Mg is used for the production of high-strength cylinder head castings. The alloy is unique for its specific low permitted Ti content (0.03 wt% max), which makes it impossible to refine the grain structure of this alloy using standard Al–Ti–B grain refiners. The specific chemical composition is specified by the supplier company. The aim of this paper is to find a suitable alloying element that would improve the selected properties (e.g., mechanical, and physical properties) that are crucial for cylinder head castings. The research focuses on the investigation of the effect of different Zr addition (0.05; 0.10; 0.15 and 0.20 wt% Zr in the form of AlZr20 master alloy) on the properties of AlSi5Cu2Mg in the as-cast state and after heat treatment T7. The obtained results showed that ultimate tensile strength, yield strength, hardness, and physical properties of as-cast samples do not change significantly with increasing Zr content. The experimental alloys showed a more significant increase in ultimate tensile strength, yield strength, hardness, and thermal conductivity after heat treatment T7. Zirconium-rich intermetallic phases were observed in the shape of separate thick needles or as a cluster of two crossed thinner needles.

The presented article includes a summary of the experimental works regarding the possibility of using and replacing more expensive primary alloys with secondary alloys. Although the use of secondary alloys is relatively widespread today, they ...

This article describes the impact of the metal mould temperature change in eliminating the adverse effect of iron in the AlSi7Mg0.3 alloy. The kind of phases based on iron to be formed in aluminium alloys is determined by the alloy chemical composition, the melt overheating temperature prior to casting, and the cooling rate during crystallisation. In the experiment, we used three various mould temperatures, and their impact on the possible change in the adverse Al₅FeSi phase, excreted in a needle form to a more compact form of Chinese writing or skeleton units. The experimental part did not use melt overheat that would result in impairment of the melt, for example due to increased gassing of the melt, as well as in a greater load on the smelting unit, thus resulting in increased energy expenditure. We can conclude from the obtained results that the mould temperature change does not have an adequate effect in eliminating the adverse effect of iron in Al-Si-Mg alloys.

The aim of the paper is to describe and specify the properties and microstructure of Al-Si alloy using Zr, a combination of Zr with elements used in the grafting of Al (Ti) alloys, and modification (Sr). Al-Si alloys with a combination of Zr and Ti and Sr elements represent an opportunity for the development of new aluminum alloys with a specific use. The experiment focused on the analysis of the synergistic effects of Zr with Ti and Zr with Sr on a AlSi7Mg0.3Cu0.5 alloy. The experimental alloys contained a constant Zr content of 0.15 wt. % and were alloyed with a gradual addition of Ti and Sr in the range of 0.1 to 0.3 wt. % for Ti, and 0.1 to 0.3 wt. % for Sr. The experimental samples were cast by meltable model casting technology. In variants with a constant addition of Zr 0.15 wt. % and a gradual addition of Ti, we observed an increase in the values of mechanical characteristics, with a significant decrease in ductility. When evaluating the structure of experimental alloys, Ti affected it by increasing the number of precipitated Zr phases. Experimental alloys with Zr and Sr addition were characterized by nucleation of Zr phases in angular morphology. It can be concluded that the investigated elements are expected to have a positive (strengthening) effect even at higher operating temperatures.