Evolution of the crystal structure of ceramics BiFeO₃–BaTiO₃ across the morphotropic phase boundary was analyzed using the results of macroscopic measuring techniques such as X-ray diffraction, differential scanning calorimetry, and differential thermal analysis, as well as the data obtained by local scale methods of scanning probe microscopy. The obtained results allowed to specify the concentration and temperature regions of the single phase and phase coexistent regions as well as to clarify a modification of the structural parameters across the rhombohedral–cubic phase boundary. The structural data show unexpected strengthening of structural distortion specific for the rhombohedral phase, which occurs upon dopant concentration and temperature-driven phase transitions to the cubic phase. The obtained results point to the non-monotonous character of the phase evolution, which is specific for metastable phases. The compounds with metastable structural state are characterized by enhanced sensitivity to external stimuli, which significantly expands the perspectives of their particular use.

The compound BiFe_0.7Mn_0.3O₃ consisting at room temperature of coexistent anti-polar orthorhombic and polar rhombohedral phases has a metastable structural state, which has been studied by laboratory X-ray, synchrotron and neutron diffraction, magnetometry, differential thermal analysis, and differential scanning calorimetry. Thermal annealing of the sample at temperatures above the temperature-driven phase transition into the single phase rhombohedral structure (~700 K) causes an increase of the volume fraction of the rhombohedral phase at room temperature from ~10% up to ~30%, which is accompanied by the modification of the magnetic state, leading to strengthening of a ferromagnetic component. A strong external magnetic field (~5 T) applied to the sample notably changes its magnetic properties, as well as provides a reinforcement of the ferromagnetic component, thus leading to an interaction between two magnetic subsystems formed by the antiferromagnetic matrix with non-collinear alignment of magnetic moments and the nanoscale ferromagnetic clusters coexisting within it. The modification of the structural state and magnetic properties of the compounds and a correlation between different structural and magnetic phases are discussed focusing on the effect of thermal annealing and the impact of an external magnetic field.

The structural state and crystal structure of Lu_(1−x)Sc_xFeO₃ (0 ≤ x ≤ 1) compounds prepared by a chemical route based on a modified sol–gel method were investigated using X-ray diffraction, Raman spectroscopy, as well as scanning electron microscopy. It was observed that chemical doping with Sc ions led to a structural phase transition from the orthorhombic structure to the hexagonal structure via a wide two-phase concentration region of 0.1 < x < 0.45. An increase in scandium content above 80 mole% led to the stabilization of the non-perovskite bixbyite phase specific for the compound ScFeO₃. The concentration stability of the different structural phases, as well as grain morphology, were studied depending on the chemical composition and synthesis conditions. Based on the data obtained for the analyzed samples, a composition-dependent phase diagram was constructed.

The crystal structure and magnetic state of the (1 − x)BiFeO₃-(x)BiMnO₃ solid solution has been analyzed by X-ray diffraction using lab-based and synchrotron radiation facilities, magnetization measurements, differential thermal analysis, and differential scanning calorimetry. Dopant concentration increases lead to the room-temperature structural transitions from the polar-active rhombohedral phase to the antipolar orthorhombic phase, and then to the monoclinic phase accompanied by the formation of two-phase regions consisting of the adjacent structural phases in the concentration ranges 0.25 < x₁ < 0.30 and 0.50 ≤ x₂ < 0.65, respectively. The accompanied changes in the magnetic structure refer to the magnetic transitions from the modulated antiferromagnetic structure to the non-colinear antiferromagnetic structure, and then to the orbitally ordered ferromagnetic structure. The compounds with a two-phase structural state at room temperature are characterized by irreversible temperature-driven structural transitions, which favor the stabilization of high-temperature structural phases. The magnetic structure of the compounds also exhibits an irreversible temperature-induced transition, resulting in an increase of the contribution from the magnetic phase associated with the high-temperature structural phase. The relationship between the structural parameters and the magnetic state of the compounds with a metastable structure is studied and discussed depending on the chemical composition and heating prehistory.

The crystal structure of BiMnO_3+δ ceramics has been studied as a function of nominal oxygen excess and temperature using synchrotron and neutron powder diffraction, magnetometry and differential scanning calorimetry. Increase in oxygen excess leads to the structural transformations from the monoclinic structure (C2/c) to another monoclinic (P2₁/c), and then to the orthorhombic (Pnma) structure through the two-phase regions. The sequence of the structural transformations is accompanied by a modification of the orbital ordering followed by its disruption. Modification of the orbital order leads to a rearrangement of the magnetic structure of the compounds from the long-range ferromagnetic to a mixed magnetic state with antiferromagnetic clusters coexistent in a ferromagnetic matrix followed by a frustration of the long-range magnetic order. Temperature increase causes the structural transition to the nonpolar orthorhombic phase regardless of the structural state at room temperature; the orbital order is destroyed in compounds BiMnO_3+δ (δ ≤ 0.14) at temperatures above 470 °C.

The unprecedented attributes such as biocompatibility and flexibility of macromolecular piezoelectric polymer has triggered an immense interested in scientific society for their potential exploitation in implantable electronic devices. In the present article, a theoretical and experimental investigation is done to explore the polarization behavior of composite fibers based on copolymer poly-trifluoroethylene P(VDF-TrFE) and graphene oxide (GO) with varying composition of the components is explored for its possible application in bioelectronic devices. Electromechanical properties of the PVDF/GO nanofibers were investigated using piezoresponse force microscopy (PFM) method. The switching behavior, charge states, and piezoelectric response of the fibers were found to depend on the concentration of GO up to 20%. Theoretical models of PVDF chains, interacting with Graphene/GO layers has been used to explore the evolution of piezoresponse in the composite fibers. In order to compute piezoelectric coefficients, the behavior of composite in electrical fields has been modeled using software HyperChem. The experimental results are qualitatively correlated with a computed theoretical model.