The W–Cu composites with nanosized grain boundaries and high effective density were fabricated using a new fast isostatic hot pressing method. A significantly faster method was proposed for the formation of W–Cu composites in comparison to the traditional ones. The influence of both the high temperature and pressure conditions on the microstructure, structure, chemical composition, and density values were observed. It has been shown that W–Cu samples have a polycrystalline well-packed microstructure. The copper performs the function of a matrix that surrounds the tungsten grains. The W–Cu composites have mixed bcc-W (sp. gr. Im $\overline{3}$ m) and fcc-Cu (sp. gr. Fm $\overline{3}$ m) phases. The W crystallite sizes vary from 107 to 175 nm depending on the sintering conditions. The optimal sintering regimes of the W–Cu composites with the highest density value of 16.37 g/cm³ were determined. Tungsten–copper composites with thicknesses of 0.06–0.27 cm have been fabricated for the radiation protection efficiency investigation against gamma rays. It has been shown that W–Cu samples have a high shielding efficiency from gamma radiation in the 0.276–1.25 MeV range of energies, which makes them excellent candidates as materials for radiation protection.

Evolution of the crystal structure of ceramics BiFeO₃–BaTiO₃ across the morphotropic phase boundary was analyzed using the results of macroscopic measuring techniques such as X-ray diffraction, differential scanning calorimetry, and differential thermal analysis, as well as the data obtained by local scale methods of scanning probe microscopy. The obtained results allowed to specify the concentration and temperature regions of the single phase and phase coexistent regions as well as to clarify a modification of the structural parameters across the rhombohedral–cubic phase boundary. The structural data show unexpected strengthening of structural distortion specific for the rhombohedral phase, which occurs upon dopant concentration and temperature-driven phase transitions to the cubic phase. The obtained results point to the non-monotonous character of the phase evolution, which is specific for metastable phases. The compounds with metastable structural state are characterized by enhanced sensitivity to external stimuli, which significantly expands the perspectives of their particular use.

Polymer-based magnetoelectric composite materials have attracted a lot of attention due to their high potential in various types of applications as magnetic field sensors, energy harvesting, and biomedical devices. Current researches are focused on the increase in the efficiency of magnetoelectric transformation. In this work, a new strategy of arrangement of clusters of magnetic nanoparticles by an external magnetic field in PVDF and PFVD-TrFE matrixes is proposed to increase the voltage coefficient (α_ME) of the magnetoelectric effect. Another strategy is the use of 3-component composites through the inclusion of piezoelectric BaTiO₃ particles. Developed strategies allow us to increase the α_ME value from ~5 mV/cm·Oe for the composite of randomly distributed CoFe₂O₄ nanoparticles in PVDF matrix to ~18.5 mV/cm·Oe for a composite of magnetic particles in PVDF-TrFE matrix with 5%wt of piezoelectric particles. The applicability of such materials as bioactive surface is demonstrated on neural crest stem cell cultures.

Using Landau-Ginzburg-Devonshire (LGD) theory for $\mathrm{BiFe}{\mathrm{O}}_3$ dense fine-grained ceramics with quasispherical grains and nanosized intergrain spaces enriched by elastic defects, we calculated a surprisingly strong size-induced increase in the antiferromagnetic transition temperature caused by the joint action of rotomagnetic and magnetostrictive coupling. Notably, all parameters included in the LGD functional have been extracted from experiments, not assumed. Complementarily, we performed experiments for dense $\mathrm{BiFe}{\mathrm{O}}_3$ ceramics, which revealed that the shift of the antiferromagnetic transition is to $T_N\sim 690\mathrm{K}$ instead of $T_N\sim 645\mathrm{K}$ for a single crystal. To explain the result theoretically, we consider the possibility of controlling the antiferromagnetic state of multiferroic $\mathrm{BiFe}{\mathrm{O}}_3$ via biquadratic antiferrodistortive rotomagnetic, rotoelectric, magnetoelectric, and magnetostrictive couplings. According to our calculations, the highest contribution is the rotostriction contribution, while the magnetostrictive and electrostriction contributions appear smaller.

The compound BiFe_0.7Mn_0.3O₃ consisting at room temperature of coexistent anti-polar orthorhombic and polar rhombohedral phases has a metastable structural state, which has been studied by laboratory X-ray, synchrotron and neutron diffraction, magnetometry, differential thermal analysis, and differential scanning calorimetry. Thermal annealing of the sample at temperatures above the temperature-driven phase transition into the single phase rhombohedral structure (~700 K) causes an increase of the volume fraction of the rhombohedral phase at room temperature from ~10% up to ~30%, which is accompanied by the modification of the magnetic state, leading to strengthening of a ferromagnetic component. A strong external magnetic field (~5 T) applied to the sample notably changes its magnetic properties, as well as provides a reinforcement of the ferromagnetic component, thus leading to an interaction between two magnetic subsystems formed by the antiferromagnetic matrix with non-collinear alignment of magnetic moments and the nanoscale ferromagnetic clusters coexisting within it. The modification of the structural state and magnetic properties of the compounds and a correlation between different structural and magnetic phases are discussed focusing on the effect of thermal annealing and the impact of an external magnetic field.

The results of studies on the wettability properties and preparation of porous anodic alumina (PAA) membranes with a 3.3 ± 0.2 μm thickness and a variety of pore sizes are presented in this article. The wettability feature results, as well as the fabrication processing characteristics and morphology, are presented. The microstructure effect of these surfaces on wettability properties is analyzed in comparison to outer PAA surfaces. The interfacial contact angle was measured for amorphous PAA membranes as-fabricated and after a modification technique (pore widening), with pore sizes ranging from 20 to 130 nm. Different surface morphologies of such alumina can be obtained by adjusting synthesis conditions, which allows the surface properties to change from hydrophilic (contact angle is approximately 13°) to hydrophobic (contact angle is 100°). This research could propose a new method for designing functional surfaces with tunable wettability. The potential applications of ordinary alumina as multifunctional films are demonstrated.