In order to better evaluate the construction quality of asphalt pavement, nondestructive testing techniques are used to inspect newly paved asphalt mixture pavement. The proposed system for the evaluation of asphalt pavement construction quality uses three-dimensional ground-penetrating radar (GPR) and a non-nuclear density gauge. The GPR and the non-nuclear density gauge test results were used to establish a dielectric constant–porosity model by fitting. This approach can more accurately determine the dielectric constant selection scheme of the GPR based on the average value of every 10 dielectric constant data points in the length direction of the radar antenna and every three data channels in the width direction. The GPR collected the dielectric constants of the road surface based on the total reflection method and used the average value of the local dielectric constant to evaluate the construction quality of the road. The non-nuclear density gauge used the local porosity to assess the construction quality of the road. It is recommended that the two testing schemes described above be used to evaluate the quality of asphalt pavement construction. They can provide theoretical guidance for future applications in practical processes.

In the French high-modulus asphalt mixture design system, the complex modulus of the mixture under the conditions of 15 °C and 10 Hz is taken as the design index. However, in China, the dynamic modulus under the conditions of 15 °C, 10 Hz, 20 °C, 10 Hz and 45 °C, 10 Hz was taken as the stiffness modulus index of high-modulus asphalt mixture. The difference in modulus values between the two systems caused the pavement structure layer to be thicker and the construction cost to be higher in China. In order to find out the appropriate modulus value of high-modulus asphalt mixture suitable for China’s modulus parameter conditions to better carry out the reasonable design and evaluation of high-modulus asphalt mixture in China, the modulus of four types of high-modulus asphalt mixtures under the two systems through the two-point bending complex modulus test of the CRT-2PT trapezoidal beam and the SPT uniaxial compression dynamic modulus test were analyzed in this paper. Under the premise of meeting the stiffness modulus index of the French high-modulus asphalt mixture, the relationship conversion models between the dynamic modulus and complex modulus of high-modulus asphalt mixture under different temperatures were established. According to the conversion models, the design evaluation value range of dynamic modulus suitable for China’s condition was recommended. It is recommended that the dynamic modulus of China’s high-modulus asphalt mixture at 15 °C and 10 Hz is not less than 16,000 MPa, the dynamic modulus at 20 °C and 10 Hz is not less than 14,000 MPa, and the dynamic modulus at 45 °C and 10 Hz is not less than 2500 MPa. Five kinds of high-modulus asphalt mixtures used in actual road engineering were tested to verify the reliability of the recommended dynamic modulus values based on the modulus conversion model, and the results are consistent with the recommended value range of the model.

High asphalt grade and poor high-temperature performance are the primary reasons for the permanent rutting deformation of asphalt pavement. However, the low grade of asphalt and the poor low-temperature performance and fatigue life of the mixture can easily lead to the low-temperature cracking of asphalt pavement. With the rapid increase in road traffic, volume, and traffic load, the performance requirements of road asphalt materials are becoming higher and higher. High-modulus asphalt has excellent temperature stability and good fatigue resistance. However, high-modulus asphalt is expensive, so its use can greatly increase the pavement cost, restricting its wide application in road engineering. It is necessary to find an economical way to produce modified asphalt to meet the current road requirements. The aim of this study is to investigate the effects of styrene-butadiene-styrene block copolymer (SBS) and rock asphalt on the road performance of modified high-modulus asphalt, in which the replacement level of SBS and rock asphalt below 8 wt.% are compared. Apart from the conventional performance measurements, such as softening point, penetration, ductility and viscosity, thermal storage stability and rheological properties are also measured. The test results show that the composite modification of SBS and North American rock asphalt can effectively improve the high-temperature resistance and reduce the temperature sensitivity of 50# matrix asphalt, but it has no obvious improvement on its low-temperature performance. The preferred ternary blending system containing 4~6 wt.% SBS and 6~8 wt.% rock asphalt was obtained by performance analysis. It was verified that the performances of high-modulus asphalt mixture with the ternary blending asphalt above all meet the requirements of high-modulus asphalt mixture performance index.

In order to explore the influence of steel slag on the road performance of asphalt mastic and its mixtures, steel slag powder (SSP) and steel slag aggregate (SSA) were used to replace limestone mineral powder filler (MF) and natural limestone aggregate (LA) respectively to prepare asphalt mastic and mixture. A series of standardized tests including penetration, softening point, ductility, viscosity, pull-off strength, dynamic shear rheometer (DSR), and bending beam rheometer (BBR) were carried out to evaluate the performance of asphalt mastics with SSP. Meanwhile, high- and low-temperature performance, moisture stability, volumetric stability, and fatigue resistance were evaluated by wheel tracking, uniaxial penetration strength, Hamburg, three-point bending, freeze–thaw splitting, immersed Marshall stability, water immersion expansion, and two-point bending trapezoidal beam fatigue tests. The results show that compared to the asphalt mastic with MF, enhanced high-temperature deformation resistance and reduced low-temperature cracking resistance of asphalt mastic with SSP were observed, as well as superior aging resistance. The improvements in high-temperature stability, moisture resistance, and fatigue performance were confirmed for asphalt mixtures with SSP/SSA. Additionally, compromised volumetric stability and low-temperature crack resistance were found when SSP/SSA was used in mixtures. Although asphalt mixtures with SSA exhibited 257.79%–424.60% higher expansion rate after 21-day immersion than those with LA, the 3-day immersion expansion rates complied with specification limits (<1.5% per JTG F40-2004). Critical volume expansion control measures should be adopted for full-component applications of steel slag powder/aggregates due to the hydration potential of free lime (f-CaO) and magnesium oxide (MgO) in steel slag under moisture exposure.

The high-modulus asphalt mixture produced by hard asphalt has played a good role in reducing asphalt pavement rutting and improving pavement durability. It was widely used in the construction of various levels of road engineering in Europe. However, low-grade hard asphalt was rarely used in road engineering in China, and the use of hard asphalt for the design and construction of high modulus asphalt mixtures lacks sufficient engineering experience. Considering the above issues, comparative research on the performance of Chinese and French low-grade hard asphalt and mixture was carried out. In this paper, the performance of French 15# hard asphalt commonly used for EME (Enrobés à Module Elevé Class) high modulus asphalt mixture and China 15# hard asphalt was analyzed comparatively, where six typical high modulus asphalt mixtures corresponding to two low-grade hard asphalts were designed referring to the design requirements of French high modulus asphalt mixtures. The road performance of a high-modulus asphalt mixture was evaluated to verify the feasibility of its application in engineering. The research results show that the performance indicators of both Chinese and French asphalts meet the requirements of binder materials used in high modulus asphalt mixtures, and the performance of their corresponding mixtures of the two asphalts also meet the specifications of high modulus asphalt mixtures. However, the two asphalts and the performance of their corresponding mixture are slightly different. The high modulus asphalt mixture of Chinese low-grade hard bitumen can be used well in road engineering applications in China. It can strongly promote the wide application of high modulus asphalt mixture in China.

Obtaining the required homogeneity, including uniform thickness and density, is very crucial for controlling the quality of flexible asphalt layers. Although non-destructive testing (NDT) methods are time-saving and less labor-intensive, they only provide indirect measurement data under testing area conditions and strongly depend on the explanations by prediction models. In this study, in terms of the three-dimensional air-launched Ground Penetrating Radar (GPR) technique, the dielectric constant of asphalt concrete base with dry conditions in pavements was detected and calculated by different methods (the Coring Method, Reflection Amplitudes Method and Common Mid-Point Method). According to the calculated dielectric constant, the thickness and density of asphalt concrete base were further calculated and assessed. Comparing with the Coring Method, the Common Mid-Point Method was recommended to calculate dielectric constants in order to obtain reliable thickness of asphalt pavement base. Among the Birefringence, Boettcher, Linearity indicator, and Rayleigh models, the Rayleigh model was suggested to predict the density, and the predicted density exhibited a good correlation coefficient with the measured one. Furthermore, by choosing these proper calculation methods, an assessment was successfully conducted to evaluate homogeneity of a constructed field pavement in practice.