This article provides an overview of high-pressure die casting (HPDC)-related research undertaken at the EPSRC Future LiME Hub between 2015–2022. The project aimed to identify the cause of variability in the tensile ductility of die-cast structures, and to develop novel processing techniques to address this issue. Variability in tensile ductility was related to the size of large pores and non-metallic inclusions. It was proposed that these non-metallic inclusions formed during the pyrolysis of commercial plunger lubricants in the shot sleeve, and that these large pores derived from dilatational strains introduced during semi-solid deformation. Processing parameters and die design were found to significantly influence the microstructure of die-cast products, and the subsequent variability in tensile ductility. To close, recent progress on the application of intensive melt shearing to HPDC is reviewed. Intensive melt shearing was found to induce significant grain refinement in both Al and Mg alloys due to the effective dispersion of native oxide particles, and the use of these particles as heterogeneous nucleation substrates. The presence of native oxide particles also enabled the use of novel heat treatment procedures that avoided conventional issues such as surface blistering and geometrical distortion.

During solidification of metallic materials, heterogeneous nucleation occurs on substrates, either endogenous or exogenous. The potency of the substrates for nucleation is mainly dependent upon the atomic arrangements on the substrate surface, which are affected by the lattice misfit between the substrate and the nucleated solid, the surface roughness at atomic scale, and the chemical interaction between the substrates and the melt. Extensive examinations on metal/substrate (M/S) interfaces at atomic scale by the state-of-the-art aberration (Cs) corrected STEM and associated EDS and EELS have shown that alloying elements in liquid melts tend to segregate at the interfaces, leading to the formation of various 2-dimensional compounds (2DCs) or 2-dimensional solutions (2DSs), depending upon segregation behavior of the elements. For instance, Al₃Ti 2DC and Ti₂Zr 2DC at the Al/TiB₂ interface, Y₂O₃ 2DC at the Mg/MgO interface, and a Si-rich 2DS layer at Al-Si/TiB₂ interface have been identified. Such interfacial segregations significantly affect nucleation potency of the substrates, resulting in either promoting or impeding the heterogeneous nucleation process during solidification. In this paper, we present an overview of the current studies of interfacial segregation behavior, the structure and chemistry of interfaces, and their impacts on the subsequent heterogeneous nucleation and grain initiation processes. Our focus is on the advances made in the understanding of the mechanisms for nucleation and grain refinement. It is demonstrated that it is feasible to manipulate heterogeneous nucleation by modifying nucleation potency of a substrate through deliberate interfacial segregation of desirable elements, achieving effective control of the grain structure of cast metallic materials.