The ejection of the plasma plume produced by laser ablation is an important process for inducing mechanical effects. Therefore, in this paper, the characteristics of the plasma plume are investigated in order to analyze the impulse coupling mechanism with two laser spot diameters, 300 μm and 1100 μm, respectively. The impulse generated by laser irradiating the copper target was measured by the torsion pendulum, and the plasma plume was investigated using fast photography and optical emission spectroscopy. The experimental results show that the optimal laser intensity is independent of the beam spot size. However, when the laser intensity is greater than 2.8 × 10⁹ W/cm², the impulse coupling coefficient with the small beam spot starts to gradually decrease, while that with the large beam spot tends to saturate. Additionally, the stream-like structure and the semi-ellipsoid structure of the plasma plume were observed, respectively. Furthermore, the electron number density was estimated using the Stark broadening method, and the effect of the plasma plume on the impulse coupling coefficient was discussed. The results provide a technical reference for several applications including orbital debris removal with lasers, laser thrusters, and laser despinning.

In the process of pulsed laser drilling, the material properties in the heat-affected zone will change due to the thermal effect of the laser. To study the effect of this change on the material tensile strength, two lasers were used to punch the standard 6061 aluminum alloy specimens with millisecond and nanosecond pulse widths, and then the tensile test was carried out on the standard specimens with a tensile tester to measure the ultimate tensile strength of the aluminum alloy. Finally, the micro-morphology of the fracture was photographed by scanning electron microscopy (SEM), and the fracture mechanism of the aluminum alloy was analyzed. The experimental results show that the relationship between the rate of intensity change induced by the millisecond laser and the ablation area ratio is more linear than that of the nanosecond laser; with the increase of ablation area ratio, the rate of intensity changes induced by the nanosecond and millisecond lasers becomes increasingly closer; three types of fractures are produced with two types of laser ablation; the plasticity of the material rapidly decreases with laser drilling, and the main reason for decrease in plasticity was stress concentration. This study provides an important point of reference for how to ensure the strength and plasticity of the components after laser drilling.

For laser ablation micropropulsion technology with metal as the target to increase the total impulse, the effective utilization and supply of a working medium is a crucial aspect. In this research, the ablation characteristics and propulsion performance of the typical metal targets, copper and aluminum, ablated via nanosecond laser ablation are analyzed. Due to the low melting point of aluminum, the protrusion characteristics in the remelted area are more prominent. Its surface morphology has characteristics for height extremum and roughness that are higher than those of copper. Affected by the anisotropy of the rough surface, the absorbed energy decreases with increasing roughness. The impulse coupling coefficient of the metal decreases and stabilizes at about 6 μN·W⁻¹. The specific pulse of aluminum obtains a minimum value of 603.6 s at 6000 pulses and improves with increasing pulses. The propulsion parameters of copper alters slightly under various working conditions, with a maximum specific impulse of 685 s.

The current transmission and reflection laser ablation micropropulsion modes have the problem of a complex working medium supply system in engineering. Therefore, we propose large-spot laser ablation with a one-dimensional supply mode. In order to verify this ablation mode, a multipulse ablation experiment of submillimeter-scale light spots was carried out on the surface of pretreated copper and nickel under the atmosphere using an ultrafast laser with a pulse width of 290 fs and 10 ps. The results show that femtosecond laser multipulse ablation (FLMA) leads to the grain refinement of copper, the crater quality of the two metals under FLMA is better, and picosecond laser multipulse ablation (PLMA) causes the crater of nickel to form a dense remelting bulge that affects laser absorption; both metals have obvious heat-affected zones after FLMA and PLMA, the heat-affected zones of nickel are 5–10% larger than those of copper, and the ablation depth of copper is deeper. Under the same conditions, the ablation mass of copper is smaller than that of nickel, and the specific impulse performance of laser ablation micropropulsion is better.