The microstructure and strengthening-toughening mechanism of a modified 4Cr5Mo2V hot-working die steel with nitrogen (0.08% N) were investigated using hardness and toughness measurements, optical microscopy, scanning electron microscopy, X-ray diffraction experiments, transmission electron microscopy, and dilatometry. The results showed that the nitrogen addition could increase the hardness and temperability of 4Cr5Mo2V steel without toughness loss with a suitable heat treatment procedure. The fair match of high strength and toughness of the nitrogen-alloyed 4Cr5Mo2V steel is associated with the refinement of the prior austenite grain, the solution hardening of nitrogen atoms, and the increase of retained austenite. Before quenching, nitrogen tends to precipitate in the form of a large amount of undissolved finer V(C, N), imposing a stronger effect on restricting the growth of prior austenitic grains and increasing the grain refining efficiency of VC by 6.8 times according to an estimate. During the quenching process, the nitrogen decreases the M_S of the martensitic transformation, increasing retained austenite, which is a benefit for toughness. During the tempering process, some of the N atoms in M(C, N) were dissolved in the matrix, causing crystal lattice distortions, thus boosting the solution reinforcing effect. Meanwhile, the solid-dissolved nitrogen inhibits the diffusion of carbon, decreasing the growth rate of the carbides and increasing tempering resistance.

Referencing the composition of a typical Nb+Ti microalloyed steel (Q345B), two kinds of steels, one microalloyed with Sn and Sb, and the other one only microalloyed with Sb were designed to study the effects of Sn and Sb on the hot ductility of Nb+Ti microalloyed steels. The Gleeble-3500 tester was adopted to determine the high-temperature mechanical properties of the two test steels. Fracture morphologies, microstructures and interior precipitation status were analyzed by SEM, CLSM (Confocal laser scanning microscope) and EDS, respectively. Results revealed that within the range of 950–650 °C, there existed the ductility trough for the two steels, which were mainly attributed to the precipitation of TiN and Nb (C, N). Additionally, precipitation of Sn and Sb were not observed in this research and the hot ductility was not affected by the addition of Sn and Sb, as compared with the Nb+Ti microalloyed steel. Therefore, addition of a small amount of Sn and Sb (≤0.05 wt.%) to the Nb+Ti microalloyed steel is favorable due to the improvement on corrosion resistance.

The oxidation resistance of TiAl alloys is crucial for their commercial application. In this paper, a cyclic oxidation test with stable air circulation was designed to investigate the cyclic oxidation behavior of the TNM alloy and 4822 alloy at 800 °C and to analyze the phase, morphology, and thermal stress evolution of the oxide layer. The oxidation weight gain curves of both alloys are found to be in parabolic form, and the oxidation reaction orders of the TNM alloy and 4822 alloy are 2.374 and 1.838, respectively. The Nb and Mo elements enhance the antioxidant performance of the TNM alloy by inhibiting the dissolution and diffusion of oxygen, Ti, and Al atoms in the TiAl alloy. The thermal stress evolution of the two alloys during the heating and cooling phases of the cyclic oxidation process are calculated separately, and it is found that the thermal stresses in the TNM alloy are smaller than those in the 4822 alloy, while the maximum thermal stresses appear at the oxide/substrate interface rather than inside the oxide scale, which quantitatively explains the oxidation peeling resistance of the two alloys.

The hot deformation behavior of TiAl alloy is analyzed by combining the true stress–strain curve and microstructure analysis. The results show that the flow stress of TiAl alloy presents the characteristics of work hardening-dynamic softening, it increases with the increase of strain rate and decreases with the increase of temperature. Based on the true stress–strain curves, the flow stress of TiAl alloy under different deformation conditions is predicted by hyperbolic sinusoidal formula. In addition, the effects of deformation temperature and strain rate on the microstructure evolution of TiAl alloy are revealed. In the process of hot compression deformation, dynamic recrystallization and γ→α, β→α phase transformation occurs. During tensile deformation, TiAl alloy exhibits super-plasticity, which is mainly due to grain rotation and coordinated deformation of β phase.

After the hot-rolled strip is cooled by laminar flow, Cl⁻, SO^2- ₄ and Ca²⁺ in turbid ring water will remain on the surface of the steel plate, which makes the steel plate corrode during storage in a humid environment. In order to clarify the effect and mechanism of residual Ca²⁺ on the corrosion of strip, simulations were carried out by setting different Ca²⁺ concentrations in solutions containing Cl⁻ and SO^2- ₄ with different times of alternate immersion. Through the analyses of corrosion pit morphology, corrosion rate, electrochemical characteristics and corrosion products, it was found that the corrosion rate increased first and then decreased regardless of the Ca²⁺ concentration. When the Ca²⁺ concentration is 50~300 mg/L, the increase of Ca²⁺ concentration will increase the adsorption rate of the matrix and increase the corrosion pits. In addition, the corrosion rate decreases, the depth of corrosion pit becomes shallow and the polarization resistance increases due to the inhibition of the calcium salt layer, and the increase of Ca²⁺ concentration will enhance the inhibition of corrosion. When the Ca²⁺ concentration is 1000 mg/L, the denseness of the calcium salt layer is easily destroyed and the corrosion is intensified due to the large amount of adsorption of ions by the matrix.