We present the study of the biocompatibility and surface properties of titanium dioxide (TiO₂) thin films deposited by direct current magnetron sputtering. These films are deposited on a quartz substrate at room temperature and annealed with different temperatures (100, 300, 500, 800 and 1100 °C). The biocompatibility of the TiO₂ thin films is analyzed using primary cultures of dorsal root ganglion (DRG) of Wistar rats, whose neurons are incubated on the TiO₂ thin films and on a control substrate during 18 to 24 h. These neurons are activated by electrical stimuli and its ionic currents and action potential activity recorded. Through X-ray diffraction (XRD), the surface of TiO₂ thin films showed a good quality, homogeneity and roughness. The XRD results showed the anatase to rutile phase transition in TiO₂ thin films at temperatures between 500 and 1100 °C. This phase had a grain size from 15 to 38 nm, which allowed a suitable structural and crystal phase stability of the TiO₂ thin films for low and high temperature. The biocompatibility experiments of these films indicated that they were appropriated for culture of living neurons which displayed normal electrical behavior.

Cytotoxicity of titanium dioxide (TiO₂) thin films on Chinese hamster ovary (CHO-K1) cells was evaluated after 24, 48 and 72 h of culture. The TiO₂ thin films were deposited using direct current magnetron sputtering. These films were post-deposition annealed at different temperatures (300, 500 and 800 °C) toward the anatase to rutile phase transformation. The root-mean-square (RMS) surface roughness of TiO₂ films went from 2.8 to 8.08 nm when the annealing temperature was increased from 300 to 800 °C. Field emission scanning electron microscopy (FESEM) results showed that the TiO₂ films’ thickness values fell within the nanometer range (290–310 nm). Based on the results of the tetrazolium dye and trypan blue assays, we found that TiO₂ thin films showed no cytotoxicity after the aforementioned culture times at which cell viability was greater than 98%. Independently of the annealing temperature of the TiO₂ thin films, the number of CHO-K1 cells on the control substrate and on all TiO₂ thin films was greater after 48 or 72 h than it was after 24 h; the highest cell survival rate was observed in TiO₂ films annealed at 800 °C. These results indicate that TiO₂ thin films do not affect mitochondrial function and proliferation of CHO-K1 cells, and back up the use of TiO₂ thin films in biomedical science.

Composites from polystyrene with hydroxyl end groups and multiwall carbon nanotubes were fabricated to evaluate their properties. The Carbon Nanotubes (CNTs) were synthetized by chemical vapor deposition technique using ferrocene and benzene as precursors. Polystyrene with hydroxyl end groups was prepared by solution polymerization employing styrene as monomer, 2-mercaptoethanol as chain transfer agent and AIBN as initiator. Thin films were obtained by two methods: pouring into petri dishes and dip-coating slides. CNTs were characterized to identify morphology and characteristic spectroscopic signals. The polystyrene with hydroxyl end groups and composites were analyzed by SEM, FTIR, Raman and UV-vis spectroscopies, Vickers microhardness and electrical resistivity. Raman analysis demonstrated chemical interactions between CNTs and polystyrene. Results showed that resistivity and transparency decreased by increasing CNTs concentrations in composites; transmittance was about 80% with 0.8 wt% content of nanotubes. The highest Vickers hardness registered value was at 1.6 wt% CNTs concentration.