Access to safe drinking water is a human right, crucial to combat inequalities, reduce poverty and allow sustainable development. In many areas of the world, however, this right is not guaranteed, in part because of the lack of easily deployable diagnostic tools. Low-cost and simple methods to test water supplies onsite can protect vulnerable communities from the impact of contaminants in drinking water. Ideally such devices would also be easy to dispose of so as to leave no trace, or have a detrimental effect on the environment. To this aim, we here report the first paper microbial fuel cell (pMFC) fabricated by screen-printing biodegradable carbon-based electrodes onto a single sheet of paper, and demonstrate its use as a shock sensor for bioactive compounds (e.g. formaldehyde) in water. We also show a simple route to enhance the sensor performance by folding back-to-back two pMFCs electrically connected in parallel. This promising proof of concept work can lead to a revolutionizing way of testing water at point of use, which is not only green, easy-to-operate and rapid, but is also affordable to all.

2,5-Furandicarboxylic acid is a platform chemical for the production of biobased polymers and materials. This study reports the synthesis of furan oligoesters via polytransesterification of dimethyl furan-2,5-dicarboxylate and linear α, ω-aliphatic diols with chain length ranging from C2 to C12, using immobilized lipase B from Candida antarctica (Novozym 435) in dry organic solvents. Dimethyl furan-2,5-dicarboxylic acid (A) and 1,4-butanediol (B) were used as model substrates under different conditions producing a mixture of cyclic (CEOs) and linear (LEOs) ester oligomers up to decamers and dodecamers, respectively, with high yield. The size of the oligomers and distribution of the products is controlled by the initial concentration of substrates and temperature. While the shortest CEOs are the main cyclic compounds at 20 mM, the longest CEOs are formed at 175 mM. The chain length of the aliphatic diol co-monomers strongly influences the yield and the type of oligoesters formed. High substrate conversion of 90–95 % was obtained for C4–C12 diols, while in the case of ethylene glycol and 1,3-propanediol the conversion was moderate (i.e., 75 %). The product of the reaction between dimethyl furan-2,5-dicarboxylate and ethylene glycol (C2) and 1,3-propanediol (C3), respectively, consisted only of linear oligoesters. Longer oligoesters were obtained for alkyl chains higher than C4. The chain length and the abundance of oligoesters increases in the order: C2<C12<C10<C3<C8<C4 <C6. No substrate or product inhibition was observed in the production of furan-based oligoesters. The present biobased oligoesters are obtained via a green process and have potential application as macromonomers.

A novel Fourier transform infrared (FT-IR) microscopy method was developed and used to analyze the diffusion of lipase CalB in two different resins during immobilization. The method consisted of a streamlined sample preparation process and an automated transmission FT-IR microscopic measurement using a commercial benchtop device. The immobilization of CalB was performed on a hydrophobic resin containing aromatic groups (ECR1030M based on divinylbenzene) and on a hydrophilic resin containing ester groups and thus oxygen (ECR8204M based on methacrylate) and FT-IR revealed that the kinetic of immobilization and the distribution of the enzyme on the two resins were completely different. Furthermore, the technique revealed that CalB was immobilized on the external surface only in the case of the hydrophobic ECR1030M in a layer of about 50–70 µm, whereas when immobilized on the hydrophilic carrier ECR8204M the interaction of the enzyme with the carrier was uniform over the full diameter of the polymer bead. The enzyme activity however was higher on the hydrophobic support ECR1030M.

Thin films of cellulose and cellulose–CaSiO₃ composites were prepared using 1-ethyl-3-methylimidazolium acetate (EMIMAc) as the dissolution medium and the composites were regenerated from an anti-solvent. The surface hydrophilicity of the resultant cellulose composites was lowered by coating them with three different hydrophobizing agents, specifically, trichloro(octadecyl)silane (TOS), ethyl 2-cyanoacrylate (E2CA) and octadecylphosphonic acid (ODPA), using a simple dip-coating technique. The prepared materials were subjected to flame retardancy, water barrier, thermal, mechanical and biodegradation properties analyses. The addition of CaSiO₃ into the cellulose increased the degradation temperature and flame retardant properties of the cellulose. The water barrier property of cellulose–CaSiO₃ composites under long term water exposure completely depends on the nature of the hydrophobic agents used for the surface modification process. All of the cellulose composites behaved mechanically as a pure elastic material with a glassy state from room temperature to 250 °C, and from 20% to 70% relative humidity (RH). The presence of the CaSiO₃ filler had no effect on the elastic modulus, but it seemed to increase after the TOS surface treatment. Biodegradability of the cellulose was evaluated by enzyme treatments and the influence of CaSiO₃ and hydrophobic agents was also derived.