Nickel (Ni) and cobalt (Co) are relevant technological metals for the future of the lithium-ion battery (LIB) industry. Based on the current and projected demand for these, an increased interest in developing processing routes to exploit lateritic occurrences has been observed, as these are reported as critical raw materials for future mineral–metallurgical industry. However, the content of Ni and Co in such ores is minimal and requires impracticable mineral-processing operations for concentration before metal extraction. It was identified that information regarding the sulfation roasting of this material is scarce on what concerns the iron sulfates interaction as a function of the temperature. Based on that context, the present work has its purposes associated with the proposition of an alternative chemical pretreatment to upgrade the content of metals of technological interest in lateritic ores through a simple roast–leach process. Thus, the chemical interactions between the mineral sample and iron (III) sulfate (Fe₂(SO₄)₃) through thermodynamic simulations and experimental procedures were explored. The latter included specific water leaching practices for the selective concentration of metals. The equilibrium calculations indicate that Fe₂(SO₄)₃ and FeSO₄ tend to decompose at lower temperatures, and considering the higher stability of other metal sulfates, it could be an interesting reagent in this type of process. Regarding the experimental results, the characterization of materials indicates a recovery of Co as high as 73.4 wt.% after sulfation roasting at 500 °C followed by water leaching, with the full content of Iron (Fe) being reported in the insoluble phase. Based on these findings, the present development could be an interesting alternative to consider within operations for the chemical upgrade of cobalt in such types of mineralogical occurrences.

Vermiculite samples were impregnated with different amounts of calcium oxide by the conventional thermal heating technique and subject to CO₂ capture experiments in thermal analysis equipment. The amount of CO₂ captured by calcium oxide increased from 13 g of CO₂ per mol of CaO to 16.8 g of CO₂ per mol of CaO when the experiments were carried out with pure calcium oxide and vermiculite impregnated with CaO (1:1), respectively. Integral isoconversional methods of Kissinger-Akahira-Sunose (KAS) and Osawa-Flynn-Wall (OFW) were used for the kinetic study of the process and good correlation coefficients were achieved. The apparent activation energy values showed that for low conversions (α < 0.3) the controlling step of the process is a mixed step where the chemical reaction and the diffusion of the reagents into the vermiculite have rates of the same order of magnitude (20 kJ < E_a < 40 kJ). For higher conversions values (α > 0.3) the apparent activation energy values suggest that the slow step is a chemical step (E_a> 40 kJ). Graphical Abstract

A sample of goethite iron ore sinter feed (G_SF) was employed as a raw material in a sintering bed. This sample partially replaced hematite sinter feed (H_SF), which is currently used as raw material in a sintering plant in the state of Minas Gerais, Brazil. This substitution did not adversely affect the chemical and metallurgical proprieties of the sinter mix product, provided that the utilization of G_SF was kept below 30% in weight. Despite the higher proportion of fines in G_SF, the presence of argillaceous minerals in the sample led to an improvement in the granulation index (GI) of the sinter mix product. The GI value increased from 68.4 to 82.7% for the experiments conducted without the presence of goethite ore and with 40% of goethite ore in the sintering mix, respectively. Consequently, the qualities of both the process and the produced sinter product were not compromised. The raw materials and the various sinters produced were characterized through X-ray fluorescence (XRF) and X-ray diffraction (XRD), as well as thermal gravimetric analysis (TGA). The XRD results were used to perform a quantitative assessment of the mineral phase using the Rietveld method (RM). This technique allowed for the determination of goethite content in the studied sample, which was 35.5%. Finally, the incorporation of G_SF in the sintering bed led to a 20% reduction in the cost of raw materials.

Steel slag is a co-product of the steelmaking industry, this material is rarely used as a binder due to its low cementitious properties. Thus, it´s believed that the alkaline activation of steel slag can enable its use as a cementitious material. This work has the objective of making a systematic bibliographic review on the theme "slag melt as a precursor in activated alkali binders". To this end, the ProKnow-C method was used for the selection and analysis of relevant research on the topic. The portfolio resulted in 71 texts, mostly journals paper. Bibliometrics showed that the country with the most publications is China and the journal with the most publications is Construction and Building Materials. The critical analysis concluded that the XRD, XRF, and compressive strength tests are the most used for the characterization of the material. It is possible to establish that there are some knowledge gaps on the subject, such as better mechanical characterization and greater production of works with dosing by the one-part method.