As wearable electronic devices are becoming an integral part of modern life, there is a vast demand for safe and efficient energy storage devices to power them. While the research and development of microbatteries and supercapacitors (SCs) have significantly progressed, the latter has attracted much attention due to their excellent power density, longevity, and safety. Furthermore, SCs with a 1D fiber shape are preferred because of their ease of integration into today’s smart garments and other wearable devices. Fiber supercapacitors based on carbon nanotubes (CNT) are promising candidates with a unique 1D structure, high electrical and thermal conductivity, outstanding flexibility, excellent mechanical strength, and low gravimetric density. This review aims to serve as a comprehensive publication presenting the fundamentals and recent developments on CNT-fiber-based SCs. The first section gives a general overview of the supercapacitor types based on the charge storage mechanisms and electrode configuration, followed by the various fiber fabrication methods. The next section explores the different strategies used to enhance the electrochemical performance of these SCs, followed by a broad study on their stretchability and multifunctionality. Finally, the review presents the current performance and scalability challenges affecting the CNT-based SCs, highlighting their prospects.

The substitution of traditional copper power transmission cables with lightweight copper–carbon nanotube (Cu–CNT) composite fibers is critical for reducing the weight, fuel consumption, and CO₂ emissions of automobiles and aircrafts. Such a replacement will also allow for lowering the transmission power loss in copper cables resulting in a decrease in coal and gas consumption, and ultimately diminishing the carbon footprint. In this work, we created a lightweight Cu–CNT composite fiber through a multistep scalable process, including spinning, densification, functionalization, and double-layer copper deposition. The characterization and testing of the fabricated fiber included surface morphology, electrical conductivity, mechanical strength, crystallinity, and ampacity (current density). The electrical conductivity of the resultant composite fiber was measured to be 0.5 × 10⁶ S/m with an ampacity of 0.18 × 10⁵ A/cm². The copper-coated CNT fibers were 16 times lighter and 2.7 times stronger than copper wire, as they revealed a gravimetric density of 0.4 g/cm³ and a mechanical strength of 0.68 GPa, suggesting a great potential in future applications as lightweight power transmission cables.