Safe and long term operation of nuclear reactors is one of the most discussed challenges in nuclear power engineering. The radiation degradation of nuclear design materials limits the operational lifetime of all nuclear installations or at least decreases its safety margin. This paper is a review of experimental PALS/PLEPS studies of different nuclear reactor pressure vessel (RPV) steels investigated over last twenty years in our laboratories. Positron annihilation lifetime spectroscopy (PALS) via its characteristics (lifetimes of positrons and their intensities) provides useful information about type and density of radiation induced defects. The new results obtained on neutron-irradiated and hydrogen ions implanted German steels were compared to those from the previous studies with the aim to evaluate different processes (neutron flux/fluence, thermal treatment or content of selected alloying elements) to the microstructural changes of neutron irradiated RPV steel specimens. The possibility of substitution of neutron treatment (connected to new defects creation) via hydrogen ions implantation was analyzed as well. The same materials exposed to comparable displacement damage (dpa) introduced by neutrons and accelerated hydrogen ions shown that in the results interpretation the effect of hydrogen as a vacancy-stabilizing gas must be considered, too. This approach could contribute to future studies of nuclear fission/fusion design steels treated by high levels of neutron irradiation.

Specimens of 15Kh2MFAA steel used for reactor pressure vessels V-213 (VVER-440 reactor) were studied by positron annihilation techniques in terms of their radiation resistance and structural recovery after thermal treatment. The radiation load was simulated by experimental implantation of 500 keV H⁺ ions. The maximum radiation damage of 1 DPA was obtained across a region of 3 µm. Radiation-induced defects were investigated by coincidence Doppler broadening spectroscopy and positron lifetime spectroscopy using a conventional positron source as well as a slow positron beam. All techniques registered an accumulation of small open-volume defects (mostly mono- and di-vacancies) due to the irradiation, with an increase of the defect volume ΔV_D ≈ 2.88 × 10⁻⁸ cm⁻³. Finally, the irradiated specimens were gradually annealed at temperatures from 200 to 550 °C and analyzed in detail. The best defect recovery was found at a temperature between 450 and 475 °C, but the final defect concentration of about ΔC_D = 0.34 ppm was still higher than in the as-received specimens.

The paper is focused on the identification of critical issues with the primary circuit components based on the operational experience with the importance of saf The paper is focused on the identification of critical issues with the primary circuit components based on the operational experience with the importance of saf