Safe and long term operation of nuclear reactors is one of the most discussed challenges in nuclear power engineering. The radiation degradation of nuclear design materials limits the operational lifetime of all nuclear installations or at least decreases its safety margin. This paper is a review of experimental PALS/PLEPS studies of different nuclear reactor pressure vessel (RPV) steels investigated over last twenty years in our laboratories. Positron annihilation lifetime spectroscopy (PALS) via its characteristics (lifetimes of positrons and their intensities) provides useful information about type and density of radiation induced defects. The new results obtained on neutron-irradiated and hydrogen ions implanted German steels were compared to those from the previous studies with the aim to evaluate different processes (neutron flux/fluence, thermal treatment or content of selected alloying elements) to the microstructural changes of neutron irradiated RPV steel specimens. The possibility of substitution of neutron treatment (connected to new defects creation) via hydrogen ions implantation was analyzed as well. The same materials exposed to comparable displacement damage (dpa) introduced by neutrons and accelerated hydrogen ions shown that in the results interpretation the effect of hydrogen as a vacancy-stabilizing gas must be considered, too. This approach could contribute to future studies of nuclear fission/fusion design steels treated by high levels of neutron irradiation.

High free-volume copolymers were prepared via polycondensation with 2,3,5,6,-tetrafluoroterephthalonitrile (TFTPN) in which a portion of the 3,3,3',3'-tetramethyl-1,1'-spirobisindane (TTSBI) of PIM-1 was replaced with dibutyl anthracene maleimide (4bIII). An investigation of free volume using positron annihilation lifetime spectroscopy (PALS), and gas permeation measurements was carried out for the thin film composite copolymer membranes and compared to PIM-1. The average free volume hole size and the gas permeance of the copolymer membranes increased with decreasing TTSBI content in the copolymer.

PLEPS, operated by the Universität der Bundeswehr München, located at NEPOMUC, is a unique tool for depth profiling of defects with positron annihilation lifetime spectroscopy using a pulsed positron beam of variable energy.

This work investigates the impact of an internal electric field on the annihilation characteristics of positrons implanted in a $180\left(10\right)\mathrm{nm}$ SiO₂ layer of a Metal-Oxide-Silicon (MOS) capacitor, using Positron Annihilation Lifetime Spectroscopy (PALS). By varying the gate voltage, electric fields up to $1.72\mathrm{MV}/\mathrm{cm}$ were applied. The measurements reveal a field-dependent suppression of positronium (Ps) formation by up to $64\%$, leading to an enhancement of free positron annihilation. The increase in free positrons suggests that vacancy clusters are the dominant defect type in the oxide layer. Additionally, drift towards the SiO₂/Si interface reveals not only larger void-like defects but also a distinct population of smaller traps that are less prominent when drifting to the Al/SiO₂ interface. In total, by combining positron drift with PALS, more detailed insights into the nature and spatial distribution of defects within the SiO₂ network and in particular near the SiO₂/Si interface are obtained.